PBT/美国杜邦/6129 NC010/低粘度

PBT/美国杜邦/6129 NC010/低粘度


参考图片：
颗粒图片：

包装图片：

成品图片： 


 

 

 
Physical Properties Metric English Comments
Density  1.12 g/cc 0.0405 lb/in³  
  1.32 g/cc 0.0477 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   123300 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 123300 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  142200 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 142200 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  165000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 165000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  396400 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 396400 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  505900 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 505900 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  626100 cP
@Shear Rate 10.0 1/s,
Temperature 260 °C		 626100 cP
@Shear Rate 10.0 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  641900 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 641900 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  918900 cP
@Shear Rate 10.0 1/s,
Temperature 250 °C		 918900 cP
@Shear Rate 10.0 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  1.3929e+6 cP
@Shear Rate 10.0 1/s,
Temperature 240 °C		 1.3929e+6 cP
@Shear Rate 10.0 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  150 cm³/g 150 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.017 cm/cm 0.017 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.015 cm/cm 0.015 in/in ISO 294-4 2577
Melt Flow  10 g/10 min
@Load 2.16 kg,
Temperature 250 °C		 10 g/10 min
@Load 4.76 lb,
Temperature 482 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   0.410 MPa
@Strain 0.170 %,
Temperature 150 °C		 59.5 psi
@Strain 0.170 %,
Temperature 302 °F		 ISO 11403-1 -2
  0.680 MPa
@Strain 0.170 %,
Temperature 90.0 °C		 98.6 psi
@Strain 0.170 %,
Temperature 194 °F		 ISO 11403-1 -2
  4.10 MPa
@Strain 2.28 %,
Temperature 150 °C		 595 psi
@Strain 2.28 %,
Temperature 302 °F		 ISO 11403-1 -2
  6.67 MPa
@Strain 4.80 %,
Temperature 150 °C		 967 psi
@Strain 4.80 %,
Temperature 302 °F		 ISO 11403-1 -2
  7.25 MPa
@Strain 2.25 %,
Temperature 90.0 °C		 1050 psi
@Strain 2.25 %,
Temperature 194 °F		 ISO 11403-1 -2
  8.25 MPa
@Strain 7.41 %,
Temperature 150 °C		 1200 psi
@Strain 7.41 %,
Temperature 302 °F		 ISO 11403-1 -2
  12.07 MPa
@Strain 4.64 %,
Temperature 90.0 °C		 1751 psi
@Strain 4.64 %,
Temperature 194 °F		 ISO 11403-1 -2
  13.63 MPa
@Strain 0.430 %,
Temperature -40.0 °C		 1977 psi
@Strain 0.430 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  14.34 MPa
@Strain 1.27 %,
Temperature 40.0 °C		 2080 psi
@Strain 1.27 %,
Temperature 104 °F		 ISO 11403-1 -2
  15.07 MPa
@Strain 7.13 %,
Temperature 90.0 °C		 2186 psi
@Strain 7.13 %,
Temperature 194 °F		 ISO 11403-1 -2
  16.61 MPa
@Strain 0.700 %,
Temperature 23.0 °C		 2409 psi
@Strain 0.700 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  22.95 MPa
@Strain 0.820 %,
Temperature -20.0 °C		 3329 psi
@Strain 0.820 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  24.96 MPa
@Strain 3.64 %,
Temperature 40.0 °C		 3620 psi
@Strain 3.64 %,
Temperature 104 °F		 ISO 11403-1 -2
  27.2 MPa
@Strain 1.04 %,
Temperature 0.000 °C		 3950 psi
@Strain 1.04 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  29.39 MPa
@Strain 6.18 %,
Temperature 40.0 °C		 4263 psi
@Strain 6.18 %,
Temperature 104 °F		 ISO 11403-1 -2
  32.22 MPa
@Strain 8.75 %,
Temperature 40.0 °C		 4673 psi
@Strain 8.75 %,
Temperature 104 °F		 ISO 11403-1 -2
  45.2 MPa
@Strain 2.17 %,
Temperature 23.0 °C		 6560 psi
@Strain 2.17 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  48.4 MPa
@Strain 1.69 %,
Temperature -40.0 °C		 7020 psi
@Strain 1.69 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  51.39 MPa
@Strain 2.00 %,
Temperature -20.0 °C		 7454 psi
@Strain 2.00 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  54.78 MPa
@Strain 2.40 %,
Temperature 0.000 °C		 7945 psi
@Strain 2.40 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  65.05 MPa
@Strain 4.22 %,
Temperature 0.000 °C		 9435 psi
@Strain 4.22 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  70.55 MPa
@Strain 3.31 %,
Temperature -20.0 °C		 10230 psi
@Strain 3.31 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  71.25 MPa
@Strain 2.81 %,
Temperature -40.0 °C		 10330 psi
@Strain 2.81 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  77.04 MPa
@Strain 5.18 %,
Temperature -20.0 °C		 11170 psi
@Strain 5.18 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  87.67 MPa
@Strain 4.16 %,
Temperature -40.0 °C		 12720 psi
@Strain 4.16 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  95.86 MPa
@Strain 5.77 %,
Temperature -40.0 °C		 13900 psi
@Strain 5.77 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  58.0 MPa 8410 psi ISO 527-1/-2
Elongation at Break  >= 50 % >= 50 % Nominal; ISO 527-1/-2
Elongation at Yield  5.0 % 5.0 % ISO 527-1/-2
Tensile Modulus  2.60 GPa 377 ksi ISO 527-1/-2
  0.251 GPa
@Temperature 120 °C		 36.4 ksi
@Temperature 248 °F		 ISO 11403-1 -2
  1.162 GPa
@Temperature 40.0 °C		 168.5 ksi
@Temperature 104 °F		 ISO 11403-1 -2
  3.024 GPa
@Temperature -40.0 °C		 438.6 ksi
@Temperature -40.0 °F		 ISO 11403-1 -2
Flexural Modulus  2.40 GPa 348 ksi ISO 178
Shear Strength   0.006261 MPa
@Shear Rate 10.0 1/s,
Temperature 260 °C		 0.9081 psi
@Shear Rate 10.0 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  0.009189 MPa
@Shear Rate 10.0 1/s,
Temperature 250 °C		 1.333 psi
@Shear Rate 10.0 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  0.013929 MPa
@Shear Rate 10.0 1/s,
Temperature 240 °C		 2.0202 psi
@Shear Rate 10.0 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  0.1982 MPa
@Shear Rate 500 1/s,
Temperature 260 °C		 28.74 psi
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  0.2530 MPa
@Shear Rate 500 1/s,
Temperature 250 °C		 36.69 psi
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  0.3209 MPa
@Shear Rate 500 1/s,
Temperature 240 °C		 46.55 psi
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  0.6165 MPa
@Shear Rate 5000 1/s,
Temperature 260 °C		 89.42 psi
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  0.7110 MPa
@Shear Rate 5000 1/s,
Temperature 250 °C		 103.1 psi
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  0.8248 MPa
@Shear Rate 5000 1/s,
Temperature 240 °C		 119.6 psi
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Secant Modulus   0.43495 GPa
@Strain 7.01 %,
Temperature 40.0 °C		 63.085 ksi
@Strain 7.01 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.686 GPa
@Strain 3.64 %,
Temperature 40.0 °C		 99.5 ksi
@Strain 3.64 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.13 GPa
@Strain 1.27 %,
Temperature 40.0 °C		 164 ksi
@Strain 1.27 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.81 GPa
@Strain 5.21 %,
Temperature -40.0 °C		 262 ksi
@Strain 5.21 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.95 GPa
@Strain 3.80 %,
Temperature -20.0 °C		 282 ksi
@Strain 3.80 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.08 GPa
@Strain 2.17 %,
Temperature 23.0 °C		 302 ksi
@Strain 2.17 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.2825 GPa
@Strain 2.40 %,
Temperature 0.000 °C		 331.05 ksi
@Strain 2.40 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.37 GPa
@Strain 0.700 %,
Temperature 23.0 °C		 344 ksi
@Strain 0.700 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.4175 GPa
@Strain 3.20 %,
Temperature -40.0 °C		 350.63 ksi
@Strain 3.20 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.5695 GPa
@Strain 2.00 %,
Temperature -20.0 °C		 372.68 ksi
@Strain 2.00 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.62 GPa
@Strain 1.04 %,
Temperature 0.000 °C		 379 ksi
@Strain 1.04 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.80 GPa
@Strain 0.820 %,
Temperature -20.0 °C		 406 ksi
@Strain 0.820 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.86 GPa
@Strain 1.69 %,
Temperature -40.0 °C		 415 ksi
@Strain 1.69 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  3.17 GPa
@Strain 0.430 %,
Temperature -40.0 °C		 460 ksi
@Strain 0.430 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.550 J/cm² 2.62 ft-lb/in² ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  2500 MPa
@Time 3600 sec		 363000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  1800 MPa
@Time 3.60e+6 sec		 261000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+12 ohm 1.00e+12 ohm IEC 60093
Dielectric Strength  26.0 kV/mm 660 kV/in IEC 60243-1
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  130 µm/m-°C 72.2 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  130 µm/m-°C 72.2 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  2.09 J/g-°C 0.500 BTU/lb-°F  
Thermal Conductivity  0.250 W/m-K 1.74 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  115 °C 239 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  50.0 °C 122 °F ISO 75-1/-2
Vicat Softening Point  175 °C 347 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.900 mm		 HB
@Thickness 0.0354 in		 IEC 60695-11-10
Flame Spread  21 mm/min
@Thickness 1.00 mm		 0.83 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  22 % 22 % ISO 4589-1/-2
 
Descriptive Properties
Delivery form Pellets  
Part Marking Code >PBT< ISO 11469
Processing Coatable  
  Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Europe  
  Near East/Africa  
UL recognition UL  

聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。

⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。

⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。

⒋耐溶剂好，无应力开裂。

⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。

⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

 

 

 

 

 

 

 

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40402.html

免责声明: 本文 PBT/美国杜邦/6129 NC010/低粘度 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4