  4. PBT/美国杜邦/SK605 NC010 增强30% 本色

PBT/美国杜邦/SK605 NC010 增强30% 本色

PBT/美国杜邦/SK605 NC010 增强30% 本色
 参考图片：

颗粒图片：

x1_1.1370875747_400_300_125618

包装图片：

成品图片：


 

 

 
Physical Properties Metric English Comments
Density  1.36 g/cc 0.0491 lb/in³  
  1.53 g/cc 0.0553 lb/in³ ISO 1183
Water Absorption  0.35 %
@Thickness 2.00 mm		 0.35 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.150 %
@Thickness 2.00 mm		 0.150 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   91150 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 91150 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  107900 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 107900 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  129480 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 129480 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  274700 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 274700 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  340700 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 340700 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  424600 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 424600 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  100 cm³/g 100 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.011 cm/cm 0.011 in/in ISO 294-4 2577
Melt Flow  10 g/10 min 10 g/10 min ISO 1133
  7.0 g/10 min
@Load 2.16 kg,
Temperature 250 °C		 7.0 g/10 min
@Load 4.76 lb,
Temperature 482 °F		 cm³/10min; ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  140 MPa 20300 psi ISO 527-1/-2
Tensile Stress   8.08 MPa
@Strain 0.250 %,
Temperature 160 °C		 1170 psi
@Strain 0.250 %,
Temperature 320 °F		 ISO 11403-1 -2
  22.5 MPa
@Strain 0.250 %,
Temperature 40.0 °C		 3260 psi
@Strain 0.250 %,
Temperature 104 °F		 ISO 11403-1 -2
  24.9 MPa
@Strain 0.250 %,
Temperature 23.0 °C		 3610 psi
@Strain 0.250 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  28.9 MPa
@Strain 0.250 %,
Temperature 0.000 °C		 4190 psi
@Strain 0.250 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  30.0 MPa
@Strain 0.250 %,
Temperature -20.0 °C		 4350 psi
@Strain 0.250 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  30.7 MPa
@Strain 0.250 %,
Temperature -40.0 °C		 4450 psi
@Strain 0.250 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  30.7 MPa
@Strain 1.50 %,
Temperature 160 °C		 4450 psi
@Strain 1.50 %,
Temperature 320 °F		 ISO 11403-1 -2
  41.3 MPa
@Strain 3.00 %,
Temperature 160 °C		 5990 psi
@Strain 3.00 %,
Temperature 320 °F		 ISO 11403-1 -2
  91.7 MPa
@Strain 1.50 %,
Temperature 40.0 °C		 13300 psi
@Strain 1.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  114 MPa
@Strain 3.00 %,
Temperature 40.0 °C		 16500 psi
@Strain 3.00 %,
Temperature 104 °F		 ISO 11403-1 -2
  122 MPa
@Strain 1.50 %,
Temperature 23.0 °C		 17700 psi
@Strain 1.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  138 MPa
@Strain 1.50 %,
Temperature 0.000 °C		 20000 psi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  149 MPa
@Strain 1.50 %,
Temperature -20.0 °C		 21600 psi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  159 MPa
@Strain 1.50 %,
Temperature -40.0 °C		 23100 psi
@Strain 1.50 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  10.0 MPa
@Strain 0.175 %,
Time 3.60e+7 sec		 1450 psi
@Strain 0.175 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.126 %,
Time 36000 sec		 1450 psi
@Strain 0.126 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.115 %,
Time 3600 sec		 1450 psi
@Strain 0.115 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.142 %,
Time 360000 sec		 1450 psi
@Strain 0.142 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.159 %,
Time 3.60e+6 sec		 1450 psi
@Strain 0.159 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  40.0 MPa
@Strain 0.603 %,
Time 360000 sec		 5800 psi
@Strain 0.603 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 0.889 %,
Time 3.60e+6 sec		 7250 psi
@Strain 0.889 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 0.682 %,
Time 36000 sec		 7250 psi
@Strain 0.682 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 1.02 %,
Time 3.60e+7 sec		 7250 psi
@Strain 1.02 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  60.0 MPa
@Strain 0.768 %,
Time 3600 sec		 8700 psi
@Strain 0.768 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  80.0 MPa
@Strain 1.53 %,
Time 360000 sec		 11600 psi
@Strain 1.53 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
Elongation at Break  2.7 % 2.7 % ISO 527-1/-2
Tensile Modulus  10.0 GPa 1450 ksi ISO 527-1/-2
  3.59 GPa
@Temperature 150 °C		 520 ksi
@Temperature 302 °F		 ISO 11403-1 -2
  4.20 GPa
@Temperature 90.0 °C		 610 ksi
@Temperature 194 °F		 Dynamic; ISO 11403-1 -2
  4.78 GPa
@Temperature 90.0 °C		 693 ksi
@Temperature 194 °F		 ISO 11403-1 -2
  7.65 GPa
@Temperature 40.0 °C		 1110 ksi
@Temperature 104 °F		 ISO 11403-1 -2
  10.5 GPa
@Temperature -40.0 °C		 1520 ksi
@Temperature -40.0 °F		 Dynamic; ISO 11403-1 -2
  10.66 GPa
@Temperature -40.0 °C		 1546 ksi
@Temperature -40.0 °F		 ISO 11403-1 -2
Flexural Strength  200 MPa 29000 psi ISO 178
Flexural Modulus  9.00 GPa 1310 ksi ISO 178
Shear Modulus   0.550 GPa
@Temperature 160 °C		 79.8 ksi
@Temperature 320 °F		 Dynamic; ISO 11403-1 -2
  0.696 GPa
@Temperature 120 °C		 101 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  1.00 GPa
@Temperature 70.0 °C		 145 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  1.94 GPa
@Temperature 20.0 °C		 281 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  2.09 GPa
@Temperature -20.0 °C		 303 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  2.21 GPa
@Temperature -50.0 °C		 321 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   1.82 GPa
@Strain 3.50 %,
Temperature 100 °C		 264 ksi
@Strain 3.50 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.99 GPa
@Strain 3.50 %,
Temperature 80.0 °C		 289 ksi
@Strain 3.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  2.95 GPa
@Strain 1.50 %,
Temperature 100 °C		 428 ksi
@Strain 1.50 %,
Temperature 212 °F		 ISO 11403-1 -2
  3.29 GPa
@Strain 3.50 %,
Temperature 40.0 °C		 477 ksi
@Strain 3.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  3.30 GPa
@Strain 1.50 %,
Temperature 80.0 °C		 479 ksi
@Strain 1.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  4.44 GPa
@Strain 0.250 %,
Temperature 100 °C		 644 ksi
@Strain 0.250 %,
Temperature 212 °F		 ISO 11403-1 -2
  4.84 GPa
@Strain 0.250 %,
Temperature 80.0 °C		 702 ksi
@Strain 0.250 %,
Temperature 176 °F		 ISO 11403-1 -2
  6.11 GPa
@Strain 1.50 %,
Temperature 40.0 °C		 887 ksi
@Strain 1.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  8.13 GPa
@Strain 1.50 %,
Temperature 23.0 °C		 1180 ksi
@Strain 1.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  9.00 GPa
@Strain 0.250 %,
Temperature 40.0 °C		 1310 ksi
@Strain 0.250 %,
Temperature 104 °F		 ISO 11403-1 -2
  9.20 GPa
@Strain 1.50 %,
Temperature 0.000 °C		 1330 ksi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  9.93 GPa
@Strain 1.50 %,
Temperature -20.0 °C		 1440 ksi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  9.96 GPa
@Strain 0.250 %,
Temperature 23.0 °C		 1440 ksi
@Strain 0.250 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  10.6 GPa
@Strain 1.50 %,
Temperature -40.0 °C		 1540 ksi
@Strain 1.50 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  11.56 GPa
@Strain 0.250 %,
Temperature 0.000 °C		 1677 ksi
@Strain 0.250 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  12.0 GPa
@Strain 0.250 %,
Temperature -20.0 °C		 1740 ksi
@Strain 0.250 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  12.28 GPa
@Strain 0.250 %,
Temperature -40.0 °C		 1781 ksi
@Strain 0.250 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  11.0 kJ/m² 5.23 ft-lb/in² ISO 180/1A
  10.0 kJ/m²
@Temperature -30.0 °C		 4.76 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
  10.0 kJ/m²
@Temperature -40.0 °C		 4.76 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  60.0 kJ/m² 28.6 ft-lb/in² ISO 180/1U
  55.0 kJ/m²
@Temperature -30.0 °C		 26.2 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
  55.0 kJ/m²
@Temperature -40.0 °C		 26.2 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1U
Charpy Impact Unnotched  7.00 J/cm² 33.3 ft-lb/in² ISO 179/1eU
  7.50 J/cm²
@Temperature -30.0 °C		 35.7 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
  7.50 J/cm²
@Temperature -40.0 °C		 35.7 ft-lb/in²
@Temperature -40.0 °F		 ISO 179/1eU
Charpy Impact, Notched  1.10 J/cm² 5.23 ft-lb/in² ISO 179/1eA
  1.00 J/cm²
@Temperature -40.0 °C		 4.76 ft-lb/in²
@Temperature -40.0 °F		 ISO 179/1eA
  1.10 J/cm²
@Temperature -30.0 °C		 5.23 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   2500 MPa
@Pressure 35.0 MPa,
Temperature 120 °C		 363000 psi
@Pressure 5080 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2520 MPa
@Pressure 30.0 MPa,
Temperature 120 °C		 365000 psi
@Pressure 4350 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2540 MPa
@Pressure 25.0 MPa,
Temperature 120 °C		 368000 psi
@Pressure 3630 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2560 MPa
@Pressure 20.0 MPa,
Temperature 120 °C		 372000 psi
@Pressure 2900 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2590 MPa
@Pressure 15.0 MPa,
Temperature 120 °C		 375000 psi
@Pressure 2180 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2600 MPa
@Pressure 10.0 MPa,
Temperature 120 °C		 378000 psi
@Pressure 1450 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2620 MPa
@Pressure 5.00 MPa,
Temperature 120 °C		 379000 psi
@Pressure 725 psi,
Temperature 248 °F		 ISO 11403-1 -2
  7270 MPa
@Pressure 80.0 MPa,
Temperature 23.0 °C		 1.05e+6 psi
@Pressure 11600 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7518.8 MPa
@Pressure 70.0 MPa,
Temperature 23.0 °C		 1.0905e+6 psi
@Pressure 10200 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7812.5 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 1.1331e+6 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  8120 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 1.18e+6 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  8460 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 1.23e+6 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  8700 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 1.26e+6 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  8740 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 1.27e+6 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  8800 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 1.28e+6 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  9000 MPa
@Time 3600 sec		 1.31e+6 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours   1720 MPa
@Pressure 50.0 MPa,
Temperature 90.0 °C		 249000 psi
@Pressure 7250 psi,
Temperature 194 °F		 ISO 11403-1 -2
  1940 MPa
@Pressure 40.0 MPa,
Temperature 90.0 °C		 282000 psi
@Pressure 5800 psi,
Temperature 194 °F		 ISO 11403-1 -2
  2130 MPa
@Pressure 35.0 MPa,
Temperature 120 °C		 310000 psi
@Pressure 5080 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2150 MPa
@Pressure 30.0 MPa,
Temperature 120 °C		 312000 psi
@Pressure 4350 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2170 MPa
@Pressure 25.0 MPa,
Temperature 120 °C		 314000 psi
@Pressure 3630 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2190 MPa
@Pressure 20.0 MPa,
Temperature 120 °C		 317000 psi
@Pressure 2900 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2210 MPa
@Pressure 15.0 MPa,
Temperature 120 °C		 320000 psi
@Pressure 2180 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2220 MPa
@Pressure 10.0 MPa,
Temperature 120 °C		 322000 psi
@Pressure 1450 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2230 MPa
@Pressure 5.00 MPa,
Temperature 120 °C		 324000 psi
@Pressure 725 psi,
Temperature 248 °F		 ISO 11403-1 -2
  2270 MPa
@Pressure 30.0 MPa,
Temperature 90.0 °C		 329000 psi
@Pressure 4350 psi,
Temperature 194 °F		 ISO 11403-1 -2
  2720 MPa
@Pressure 20.0 MPa,
Temperature 90.0 °C		 394000 psi
@Pressure 2900 psi,
Temperature 194 °F		 ISO 11403-1 -2
  3460 MPa
@Pressure 10.0 MPa,
Temperature 90.0 °C		 502000 psi
@Pressure 1450 psi,
Temperature 194 °F		 ISO 11403-1 -2
  4260 MPa
@Pressure 80.0 MPa,
Temperature 23.0 °C		 617000 psi
@Pressure 11600 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  4860 MPa
@Pressure 70.0 MPa,
Temperature 23.0 °C		 705000 psi
@Pressure 10200 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5310 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 770000 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5624.3 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 815740 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5910 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 858000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6120 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 887000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6190 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 898000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6290 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 912000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6600 MPa
@Time 3.60e+6 sec		 957000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm IEC 60093
Dielectric Constant   3.8
@Frequency 1.00e+6 Hz		 3.8
@Frequency 1.00e+6 Hz		 IEC 60250
  4.4
@Frequency 100 Hz		 4.4
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  31.0 kV/mm 787 kV/in IEC 60243-1
Dissipation Factor   0.0020
@Frequency 1000 Hz		 0.0020
@Frequency 1000 Hz		 ASTM D150
  0.0025
@Frequency 100 Hz		 0.0025
@Frequency 100 Hz		 IEC 60250
  0.018
@Frequency 1.00e+6 Hz		 0.018
@Frequency 1.00e+6 Hz		 IEC 60250
  0.018
@Frequency 1.00e+6 Hz		 0.018
@Frequency 1.00e+6 Hz		 ASTM D150
Comparative Tracking Index  450 V 450 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  30.0 µm/m-°C 16.7 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  90.0 µm/m-°C 50.0 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.73 J/g-°C 0.413 BTU/lb-°F  
Thermal Conductivity  0.280 W/m-K 1.94 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  205 °C 401 °F ISO 75-1/-2
Vicat Softening Point  215 °C 419 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Flame Spread  41 mm/min
@Thickness 1.00 mm		 1.6 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  19 % 19 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Fogging 99% ISO 6452; F-value (refraction)
Part Marking Code >PBT-GF30< ISO 11469
Processing Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-GF30  
UL recognition UL  

聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。

⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。

⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。

⒋耐溶剂好，无应力开裂。

⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。

⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40450.html

免责声明: 本文 PBT/美国杜邦/SK605 NC010 增强30% 本色 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4