类别：聚合物；热塑性塑料；尼龙
材料说明：Grivory gvs-5h黑9915是50%的玻璃纤维增强的热塑性工程塑料材料的基础上结合半结晶聚酰胺部分芳族共聚酰胺。
Grivory gvs-5h黑9915是用于注射成型技术的零件表面质量好，具有出色的特性，即使在水分的吸收：高刚度和强度，尺寸稳定性，低翘曲，良好的耐化学性，良好的表面光洁度
Grivory gvs-5h黑9915是用于注射成型技术的零件表面质量好，具有出色的特性，即使在水分的吸收：高刚度和强度，尺寸稳定性，低翘曲，良好的耐化学性，良好的表面光洁度
Grivory gvs-5h黑9915是压铸合金的经济选择。它适用于生产技术领域中的应用领域：电器/电子，汽车，安全技术，机械工程，家用电器
物性表:| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.0 % | 4.0 % | ISO 62 | ||
| Moisture Absorption | 1.40 % | 1.40 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 255 MPa | 37000 psi | conditioned; ISO 2039-1 | ||
| 280 MPa | 40600 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 220 MPa | 31900 psi | conditioned; ISO 527-1/-2 | ||
| 250 MPa | 36300 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 | ||
| 2.5 % | 2.5 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 16.0 GPa | 2320 ksi | conditioned; ISO 527-1/-2 | ||
| 17.0 GPa | 2470 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | conditioned; ISO 179/1eU | ||
| 9.00 J/cm² | 42.8 ft-lb/in² | dry; ISO 179/1eU | |||
| 6.00 J/cm² @Temperature 30.0 °C |
28.6 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |||
| 7.50 J/cm² @Temperature 30.0 °C |
35.7 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | dry; ISO 179/1eA | ||
| 1.50 J/cm² | 7.14 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 1.50 J/cm² @Temperature 30.0 °C |
7.14 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |||
| 1.50 J/cm² @Temperature 30.0 °C |
7.14 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | ||
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | conditioned; IEC 60093 | |||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | dry; IEC 60243-1 | ||
| 33.0 kV/mm | 838 kV/in | conditioned; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C | 8.33 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 100 - 120 °C | 212 - 248 °F | long term; EMS | ||
| 220 °C | 428 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 185 °C | 365 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| De |
|||||
| Automotive | Air intake sytems | ||||
| Automotive electr. and electronics, lighting | |||||
| Cooling and climate control | |||||
| Exterior | |||||
| Interior | |||||
| Powertrain and Chassis | |||||
| Electricals & Electronics | Electrical appliances | ||||
| Electrical equipment | |||||
| Energy distribution | |||||
| Mobile phones and other portable devices | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Housewares | ||||
| Hydraulics & Pneumatics | |||||
| Mechanical Engineering | |||||
| Power transmission | |||||
| Sanitary, water and gas supply | |||||
| Sports & Leisure | |||||
| Tools & Accessories | |||||
| Processing | Injection Molding | ||||
| Product Attributes | Partially aromatic Polyamide | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com