  4. PBT/美国杜邦/SK645FR NC010 强度高、耐疲劳

PBT/美国杜邦/SK645FR NC010 强度高、耐疲劳

PBT/美国杜邦/SK645FR NC010 强度高、耐疲劳
 参考图片：

颗粒图片：

100013567048_14032739394852

包装图片：

成品图片：

8-1031642-801394

 

 

 

Physical Properties Metric English Comments
Density  1.49 g/cc 0.0538 lb/in³  
  1.71 g/cc 0.0618 lb/in³ ISO 1183
Water Absorption  0.30 %
@Thickness 2.00 mm		 0.30 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.100 %
@Thickness 2.00 mm		 0.100 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   110800 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 110800 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  124700 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 124700 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  141400 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 141400 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  348200 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 348200 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  405300 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 405300 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  473400 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 473400 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in ISO 294-4 2577
  0.0050 cm/cm 0.0050 in/in annealed; ISO 294-4
Linear Mold Shrinkage, Transverse  0.012 cm/cm 0.012 in/in ISO 294-4 2577
  0.015 cm/cm 0.015 in/in annealed; ISO 294-4
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  125 MPa 18100 psi ISO 527-1/-2
Tensile Stress   9.09 MPa
@Strain 0.250 %,
Temperature 150 °C		 1320 psi
@Strain 0.250 %,
Temperature 302 °F		 ISO 11403-1 -2
  14.1 MPa
@Strain 0.250 %,
Temperature 90.0 °C		 2050 psi
@Strain 0.250 %,
Temperature 194 °F		 ISO 11403-1 -2
  22.615 MPa
@Strain 0.260 %,
Temperature 40.0 °C		 3280.0 psi
@Strain 0.260 %,
Temperature 104 °F		 ISO 11403-1 -2
  23.34 MPa
@Strain 0.840 %,
Temperature 160 °C		 3385 psi
@Strain 0.840 %,
Temperature 320 °F		 ISO 11403-1 -2
  26.12 MPa
@Strain 0.215 %,
Temperature -20.0 °C		 3788 psi
@Strain 0.215 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  28.13 MPa
@Strain 0.225 %,
Temperature -40.0 °C		 4080 psi
@Strain 0.225 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  30.115 MPa
@Strain 0.265 %,
Temperature 23.0 °C		 4367.8 psi
@Strain 0.265 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  30.365 MPa
@Strain 0.265 %,
Temperature 0.000 °C		 4404.1 psi
@Strain 0.265 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  34.5 MPa
@Strain 1.50 %,
Temperature 150 °C		 5000 psi
@Strain 1.50 %,
Temperature 302 °F		 ISO 11403-1 -2
  34.61 MPa
@Strain 1.68 %,
Temperature 160 °C		 5020 psi
@Strain 1.68 %,
Temperature 320 °F		 ISO 11403-1 -2
  39.16 MPa
@Strain 2.30 %,
Temperature 160 °C		 5680 psi
@Strain 2.30 %,
Temperature 320 °F		 ISO 11403-1 -2
  42.25 MPa
@Strain 2.92 %,
Temperature 160 °C		 6128 psi
@Strain 2.92 %,
Temperature 320 °F		 ISO 11403-1 -2
  43.8 MPa
@Strain 3.00 %,
Temperature 150 °C		 6350 psi
@Strain 3.00 %,
Temperature 302 °F		 ISO 11403-1 -2
  56.1 MPa
@Strain 1.50 %,
Temperature 90.0 °C		 8140 psi
@Strain 1.50 %,
Temperature 194 °F		 ISO 11403-1 -2
  69.7 MPa
@Strain 3.00 %,
Temperature 90.0 °C		 10100 psi
@Strain 3.00 %,
Temperature 194 °F		 ISO 11403-1 -2
  89.325 MPa
@Strain 1.48 %,
Temperature 40.0 °C		 12956 psi
@Strain 1.48 %,
Temperature 104 °F		 ISO 11403-1 -2
  115.2 MPa
@Strain 1.485 %,
Temperature 23.0 °C		 16710 psi
@Strain 1.485 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  127.31 MPa
@Strain 1.485 %,
Temperature 0.000 °C		 18465 psi
@Strain 1.485 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  137.8 MPa
@Strain 1.50 %,
Temperature -20.0 °C		 19980 psi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  146.5 MPa
@Strain 1.52 %,
Temperature -40.0 °C		 21250 psi
@Strain 1.52 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  15.0 MPa
@Strain 0.130 %,
Time 3600 sec		 2180 psi
@Strain 0.130 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  15.0 MPa
@Strain 0.150 %,
Time 36000 sec		 2180 psi
@Strain 0.150 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  15.0 MPa
@Strain 0.170 %,
Time 360000 sec		 2180 psi
@Strain 0.170 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  30.0 MPa
@Strain 0.400 %,
Time 3.60e+6 sec		 4350 psi
@Strain 0.400 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
Elongation at Break  2.4 % 2.4 % ISO 527-1/-2
Tensile Modulus  11.2 GPa 1620 ksi ISO 527-1/-2
  4.165 GPa
@Temperature 120 °C		 604.1 ksi
@Temperature 248 °F		 ISO 11403-1 -2
  8.079 GPa
@Temperature 40.0 °C		 1172 ksi
@Temperature 104 °F		 ISO 11403-1 -2
  11.662 GPa
@Temperature -40.0 °C		 1691.4 ksi
@Temperature -40.0 °F		 ISO 11403-1 -2
Flexural Strength  215 MPa 31200 psi ISO 178
Secant Modulus   2.20 GPa
@Strain 2.88 %,
Temperature 100 °C		 319 ksi
@Strain 2.88 %,
Temperature 212 °F		 ISO 11403-1 -2
  2.69 GPa
@Strain 2.16 %,
Temperature 100 °C		 391 ksi
@Strain 2.16 %,
Temperature 212 °F		 ISO 11403-1 -2
  3.3469 GPa
@Strain 1.45 %,
Temperature 100 °C		 485.43 ksi
@Strain 1.45 %,
Temperature 212 °F		 ISO 11403-1 -2
  4.25 GPa
@Strain 1.50 %,
Temperature 80.0 °C		 616 ksi
@Strain 1.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  4.3137 GPa
@Strain 0.730 %,
Temperature 100 °C		 625.66 ksi
@Strain 0.730 %,
Temperature 212 °F		 ISO 11403-1 -2
  5.215 GPa
@Strain 0.200 %,
Temperature 100 °C		 756.4 ksi
@Strain 0.200 %,
Temperature 212 °F		 ISO 11403-1 -2
  6.04 GPa
@Strain 1.48 %,
Temperature 40.0 °C		 875 ksi
@Strain 1.48 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.20 GPa
@Strain 0.250 %,
Temperature 80.0 °C		 899 ksi
@Strain 0.250 %,
Temperature 176 °F		 ISO 11403-1 -2
  7.76 GPa
@Strain 1.485 %,
Temperature 23.0 °C		 1130 ksi
@Strain 1.485 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  8.57 GPa
@Strain 1.485 %,
Temperature 0.000 °C		 1240 ksi
@Strain 1.485 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  8.70 GPa
@Strain 0.260 %,
Temperature 40.0 °C		 1260 ksi
@Strain 0.260 %,
Temperature 104 °F		 ISO 11403-1 -2
  9.18 GPa
@Strain 1.50 %,
Temperature -20.0 °C		 1330 ksi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  9.64 GPa
@Strain 1.52 %,
Temperature -40.0 °C		 1400 ksi
@Strain 1.52 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  11.4 GPa
@Strain 0.265 %,
Temperature 23.0 °C		 1650 ksi
@Strain 0.265 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  11.5 GPa
@Strain 0.265 %,
Temperature 0.000 °C		 1660 ksi
@Strain 0.265 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  12.1 GPa
@Strain 0.215 %,
Temperature -20.0 °C		 1760 ksi
@Strain 0.215 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  12.5 GPa
@Strain 0.225 %,
Temperature -40.0 °C		 1810 ksi
@Strain 0.225 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  9.00 kJ/m² 4.28 ft-lb/in² ISO 180/1A
  8.00 kJ/m²
@Temperature -30.0 °C		 3.81 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  40.0 kJ/m² 19.0 ft-lb/in² ISO 180/1U
  40.0 kJ/m²
@Temperature -30.0 °C		 19.0 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  5.30 J/cm² 25.2 ft-lb/in² ISO 179/1eU
  5.70 J/cm²
@Temperature -30.0 °C		 27.1 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.910 J/cm² 4.33 ft-lb/in² ISO 179/1eA
  0.940 J/cm²
@Temperature -30.0 °C		 4.47 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   4687.5 MPa
@Pressure 30.0 MPa,
Temperature 100 °C		 679870 psi
@Pressure 4350 psi,
Temperature 212 °F		 ISO 11403-1 -2
  4830 MPa
@Pressure 25.0 MPa,
Temperature 100 °C		 700000 psi
@Pressure 3630 psi,
Temperature 212 °F		 ISO 11403-1 -2
  5000 MPa
@Pressure 20.0 MPa,
Temperature 100 °C		 725000 psi
@Pressure 2900 psi,
Temperature 212 °F		 ISO 11403-1 -2
  5170 MPa
@Pressure 15.0 MPa,
Temperature 100 °C		 750000 psi
@Pressure 2180 psi,
Temperature 212 °F		 ISO 11403-1 -2
  5260 MPa
@Pressure 5.00 MPa,
Temperature 100 °C		 763000 psi
@Pressure 725 psi,
Temperature 212 °F		 ISO 11403-1 -2
  5270 MPa
@Pressure 10.0 MPa,
Temperature 100 °C		 764000 psi
@Pressure 1450 psi,
Temperature 212 °F		 ISO 11403-1 -2
  8700 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 1.26e+6 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  9210 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 1.34e+6 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  9910 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 1.44e+6 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  10700 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 1.55e+6 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  11300 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 1.64e+6 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  11700 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 1.69e+6 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  11000 MPa
@Time 3600 sec		 1.60e+6 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours   3125 MPa
@Pressure 30.0 MPa,
Temperature 100 °C		 453200 psi
@Pressure 4350 psi,
Temperature 212 °F		 ISO 11403-1 -2
  3150 MPa
@Pressure 25.0 MPa,
Temperature 100 °C		 457000 psi
@Pressure 3630 psi,
Temperature 212 °F		 ISO 11403-1 -2
  3190 MPa
@Pressure 20.0 MPa,
Temperature 100 °C		 462000 psi
@Pressure 2900 psi,
Temperature 212 °F		 ISO 11403-1 -2
  3230 MPa
@Pressure 15.0 MPa,
Temperature 100 °C		 468000 psi
@Pressure 2180 psi,
Temperature 212 °F		 ISO 11403-1 -2
  3280 MPa
@Pressure 10.0 MPa,
Temperature 100 °C		 476000 psi
@Pressure 1450 psi,
Temperature 212 °F		 ISO 11403-1 -2
  3330 MPa
@Pressure 5.00 MPa,
Temperature 100 °C		 483000 psi
@Pressure 725 psi,
Temperature 212 °F		 ISO 11403-1 -2
  6590 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 956000 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6830 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 991000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7150 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 1.04e+6 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7500 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 1.09e+6 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7800 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 1.13e+6 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7990 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 1.16e+6 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  8000 MPa
@Time 3.60e+6 sec		 1.16e+6 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm IEC 60093
Dielectric Constant   3.8
@Frequency 1.00e+6 Hz		 3.8
@Frequency 1.00e+6 Hz		 IEC 60250
  4.5
@Frequency 100 Hz		 4.5
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  28.0 kV/mm 711 kV/in IEC 60243-1
Dissipation Factor   0.0030
@Frequency 100 Hz		 0.0030
@Frequency 100 Hz		 IEC 60250
  0.016
@Frequency 1.00e+6 Hz		 0.016
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  250 V 250 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  30.0 µm/m-°C 16.7 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  90.0 µm/m-°C 50.0 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.60 J/g-°C 0.382 BTU/lb-°F  
Thermal Conductivity  0.260 W/m-K 1.80 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  210 °C 410 °F ISO 75-1/-2
Vicat Softening Point  212 °C 414 °F 50°C/h 50N; ISO 306
Flammability, UL94   V-0
@Thickness 1.50 mm		 V-0
@Thickness 0.0591 in		 IEC 60695-11-10
  V-0
@Thickness 0.800 mm		 V-0
@Thickness 0.0315 in		 IEC 60695-11-10
Oxygen Index  31 % 31 % ISO 4589-1/-2
 
Descriptive Properties
Delivery form Pellets  
Part Marking Code >PBT-GF30FR(17)< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT-GF30FR(17)  
UL recognition UL  

聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。

⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。

⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。

⒋耐溶剂好，无应力开裂。

⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。

⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40470.html

免责声明: 本文 PBT/美国杜邦/SK645FR NC010 强度高、耐疲劳 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4