| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.90 % @Thickness 2.00 mm |
0.90 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Moisture Absorption | 0.350 % @Thickness 2.00 mm |
0.350 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Viscosity | 148000 cP @Shear Rate 5000 1/s, Temperature 220 °C |
148000 cP @Shear Rate 5000 1/s, Temperature 428 °F |
ISO 11403-1 -2 | ||
| 171000 cP @Shear Rate 5000 1/s, Temperature 205 °C |
171000 cP @Shear Rate 5000 1/s, Temperature 401 °F |
ISO 11403-1 -2 | |||
| 201000 cP @Shear Rate 5000 1/s, Temperature 190 °C |
201000 cP @Shear Rate 5000 1/s, Temperature 374 °F |
ISO 11403-1 -2 | |||
| 688000 cP @Shear Rate 500 1/s, Temperature 220 °C |
688000 cP @Shear Rate 500 1/s, Temperature 428 °F |
ISO 11403-1 -2 | |||
| 856000 cP @Shear Rate 500 1/s, Temperature 205 °C |
856000 cP @Shear Rate 500 1/s, Temperature 401 °F |
ISO 11403-1 -2 | |||
| 1.058e+6 cP @Shear Rate 500 1/s, Temperature 190 °C |
1.058e+6 cP @Shear Rate 500 1/s, Temperature 374 °F |
ISO 11403-1 -2 | |||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4 2577 | ||
| Melt Flow | 1.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
cm³/10min; ISO 1133 | ||
| 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 58 | 58 | ISO 2039-2 | ||
| Hardness, Rockwell R | 105 | 105 | ISO 2039-2 | ||
| Tensile Stress | 6.10 MPa @Strain 2.00 %, Temperature 90.0 °C |
885 psi @Strain 2.00 %, Temperature 194 °F |
ISO 11403-1 -2 | ||
| 14.3 MPa @Strain 7.90 %, Temperature 90.0 °C |
2070 psi @Strain 7.90 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 15.5 MPa @Strain 2.00 %, Temperature 40.0 °C |
2250 psi @Strain 2.00 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 16.9 MPa @Strain 13.9 %, Temperature 90.0 °C |
2450 psi @Strain 13.9 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 17.6 MPa @Strain 19.8 %, Temperature 90.0 °C |
2550 psi @Strain 19.8 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 18.3 MPa @Strain 2.10 %, Temperature 23.0 °C |
2650 psi @Strain 2.10 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 27.5 MPa @Strain 3.00 %, Temperature 0.000 °C |
3990 psi @Strain 3.00 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 29.8 MPa @Strain 7.80 %, Temperature 40.0 °C |
4320 psi @Strain 7.80 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 33.5 MPa @Strain 13.7 %, Temperature 40.0 °C |
4860 psi @Strain 13.7 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 34.6 MPa @Strain 19.5 %, Temperature 40.0 °C |
5020 psi @Strain 19.5 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 34.7 MPa @Strain 3.70 %, Temperature -20.0 °C |
5030 psi @Strain 3.70 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 35.0 MPa @Strain 8.50 %, Temperature 23.0 °C |
5080 psi @Strain 8.50 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 39.2 MPa @Strain 14.8 %, Temperature 23.0 °C |
5690 psi @Strain 14.8 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 40.3 MPa @Strain 21.2 %, Temperature 23.0 °C |
5850 psi @Strain 21.2 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 44.9 MPa @Strain 12.1 %, Temperature 0.000 °C |
6510 psi @Strain 12.1 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 47.5 MPa @Strain 21.2 %, Temperature 0.000 °C |
6890 psi @Strain 21.2 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 48.3 MPa @Strain 30.3 %, Temperature 0.000 °C |
7010 psi @Strain 30.3 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 51.6 MPa @Strain 14.8 %, Temperature -20.0 °C |
7480 psi @Strain 14.8 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 54.9 MPa @Strain 25.9 %, Temperature -20.0 °C |
7960 psi @Strain 25.9 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 56.0 MPa @Strain 34.5 %, Temperature -20.0 °C |
8120 psi @Strain 34.5 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 30 % | 30 % | ISO 527-1/-2 | ||
| Tensile Modulus | 1.40 GPa | 203 ksi | ISO 527-1/-2 | ||
| 0.363 GPa @Temperature 110 °C |
52.7 ksi @Temperature 230 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.3427 GPa @Temperature 30.0 °C |
194.74 ksi @Temperature 86.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| 2.03 GPa @Temperature -20.0 °C |
294 ksi @Temperature -4.00 °F |
Dynamic; ISO 11403-1 -2 | |||
| 5.48 GPa @Temperature -70.0 °C |
794 ksi @Temperature -94.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| 8.17 GPa @Temperature -100 °C |
1180 ksi @Temperature -148 °F |
Dynamic; ISO 11403-1 -2 | |||
| Flexural Strength | 34.0 MPa @Strain 3.50 % |
4930 psi @Strain 3.50 % |
ISO 178 | ||
| Flexural Modulus | 1.10 GPa | 160 ksi | ISO 178 | ||
| Shear Modulus | 0.0911 GPa @Temperature 120 °C |
13.2 ksi @Temperature 248 °F |
Dynamic; ISO 11403-1 -2 | ||
| 0.2153 GPa @Temperature 70.0 °C |
31.23 ksi @Temperature 158 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.4067 GPa @Temperature 20.0 °C |
58.99 ksi @Temperature 68.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| 0.6135 GPa @Temperature -20.0 °C |
88.98 ksi @Temperature -4.00 °F |
Dynamic; ISO 11403-1 -2 | |||
| 1.1443 GPa @Temperature -50.0 °C |
165.97 ksi @Temperature -58.0 °F |
Dynamic; ISO 11403-1 -2 | |||
| Secant Modulus | 0.187 GPa @Strain 29.6 %, Temperature -20.0 °C |
27.1 ksi @Strain 29.6 %, Temperature -4.00 °F |
ISO 11403-1 -2 | ||
| 0.198 GPa @Strain 24.2 %, Temperature 0.000 °C |
28.6 ksi @Strain 24.2 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 0.21859 GPa @Strain 15.6 %, Temperature 40.0 °C |
31.704 ksi @Strain 15.6 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 0.234 GPa @Strain 17.0 %, Temperature 23.0 °C |
34.0 ksi @Strain 17.0 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 0.349 GPa @Strain 14.8 %, Temperature -20.0 °C |
50.6 ksi @Strain 14.8 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 0.371 GPa @Strain 12.1 %, Temperature 0.000 °C |
53.8 ksi @Strain 12.1 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 0.382 GPa @Strain 7.80 %, Temperature 40.0 °C |
55.4 ksi @Strain 7.80 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 0.412 GPa @Strain 8.50 %, Temperature 23.0 °C |
59.7 ksi @Strain 8.50 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 0.775 GPa @Strain 2.00 %, Temperature 40.0 °C |
112 ksi @Strain 2.00 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 0.871 GPa @Strain 2.10 %, Temperature 23.0 °C |
126 ksi @Strain 2.10 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 0.917 GPa @Strain 3.00 %, Temperature 0.000 °C |
133 ksi @Strain 3.00 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 0.938 GPa @Strain 3.70 %, Temperature -20.0 °C |
136 ksi @Strain 3.70 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 90.0 kJ/m² | 42.8 ft-lb/in² | ISO 180/1A | ||
| 20.0 kJ/m² @Temperature -40.0 °C |
9.52 ft-lb/in² @Temperature -40.0 °F |
ISO 180/1A | |||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 9.00 J/cm² | 42.8 ft-lb/in² | ISO 179/1eA | ||
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 1100 MPa @Time 3600 sec |
160000 psi @Time 1.00 hour |
ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 550 MPa @Time 3.60e+6 sec |
79800 psi @Time 1000 hour |
ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.4 @Frequency 100 Hz |
4.4 @Frequency 100 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 140 µm/m-°C | 77.8 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | -35.0 °C | -31.0 °F | 10°C/min; ISO 11357-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| Flame Spread | 60 mm/min @Thickness 1.00 mm |
2.4 in/min @Thickness 0.0394 in |
ISO 3795 (FMVSS 302) | ||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Emissions | <8 mg/kg | VDA 275 | |||
| Part Marking Code | >POM-HI< | ISO 11469 | |||
| Processing | Blow Moulding | ||||
| Coatable | |||||
| Injection Moulding | |||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Sheet Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | POM-HI | ISO 1043 | |||
| UL recognition | UL | ||||
概述
pom（聚甲醛）
聚甲醛(英文：polyformaldehyde)热塑性结晶聚合物。被誉为“超钢”或者“赛钢”，又称聚氧亚甲基。英文缩写为POM。通常甲醛聚合所得之聚合物，聚合度不高，且易受热解聚。可用作有机化工、合成树脂的原料，也用作药物熏蒸剂。白色可燃结晶粉末，具有甲醛气味。 缓慢溶于冷水，在热水中溶解较快。
一般性能
聚甲醛是一种表面光滑、有光泽的硬而致密的材料，淡黄或白色，薄壁部分呈半透明。燃烧特性为容易燃烧，离火后继续燃烧，火焰上端呈黄色，下端呈蓝色，发生熔融滴落，有强烈的刺激性甲醛味、鱼腥臭。聚甲醛为白色粉末，一般不透明，着色性好，
力学性能
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。POM的冲击强度较高,POM的摩擦因数小，耐磨性好。POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。
电学性能
POM的电绝缘性较好，几乎不受温度和湿度的影响；介电常数和介电损耗在很宽的温度、湿度和频率范围内变化很小；耐电弧性极好，并可在高温下保持。POM的介电强度与厚度有关，厚度0.127mm时为82.7kV/mm，厚度为1.88mm时为23.6kV/mm。
环境性能
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。
成形性
结晶料，熔融范围窄，熔融和凝固快，料温稍低于熔融温度即发生结晶，流动性中等，吸湿小，可不经干燥处理。
优缺点
优点
1、具高机械强度和刚性；2、最高的疲劳强度；3、环境抵抗性、耐有机溶剂性佳；
4、耐反覆冲击性强；5、广泛的使用温度范围(-40℃~120℃)；6、良好的电气性质；
7、复原性良好；8、具自已润滑性、耐磨性良好；9、尺寸安定性优。
缺点
受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。
用途
多聚甲醛为高甲醛含量的固态甲醛，呈固体颗粒状、便于贮存和运输。在较高的温度下能变成甲醛蒸气，易于代替高浓度甲醛参与各种反应，有利于化工、制药等化学合成及其他工业领域的应用，特别是在要求使用无水甲醛作原料的合成方面，用途广泛。主要有以下几方面（1）农药：合成乙草胺、丁草胺和草甘膦等；（2）涂料：合成高档汽车用漆；（3）树脂：合成脲醛树脂、酚醛树脂、聚缩醛树脂、蜜胺树脂、离子交换树脂等及各种粘合剂；（4）造纸：合成纸张增强剂； （5）铸造：翻砂脱膜剂、合成铸造粘合剂；（6）养殖业：薰蒸消毒剂。（7）有机原料：用于制备季戊四醇、三羟甲基丙烷、甘油、丙烯酸、丙烯酸甲酯、甲基丙烯酸、N－羟基甲基丙烯酰胺、烷基苯酚、甲基乙烯基酮等。（8）其他：医药及消毒。
上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！
可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：
联系人：邓小姐
联系电话：13917657923
联系QQ:996152797
联系邮箱：996152797@qq.com