  4. 抗紫外线 耐老化 POM 美国杜邦 127UV NC010

抗紫外线 耐老化 POM 美国杜邦 127UV NC010

抗紫外线 耐老化 POM 美国杜邦 127UV NC010
 参考图片：

颗粒图片：
g1_14259720

包装图片：

成品图片：

 

 

 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³ ISO 1183
Water Absorption  1.2 %
@Thickness 2.00 mm		 1.2 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.300 %
@Thickness 2.00 mm		 0.300 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   138000 cP
@Shear Rate 5000 1/s,
Temperature 230 °C		 138000 cP
@Shear Rate 5000 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  147000 cP
@Shear Rate 5000 1/s,
Temperature 215 °C		 147000 cP
@Shear Rate 5000 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  157000 cP
@Shear Rate 5000 1/s,
Temperature 200 °C		 157000 cP
@Shear Rate 5000 1/s,
Temperature 392 °F		 ISO 11403-1 -2
  649000 cP
@Shear Rate 500 1/s,
Temperature 230 °C		 649000 cP
@Shear Rate 500 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  723000 cP
@Shear Rate 500 1/s,
Temperature 215 °C		 723000 cP
@Shear Rate 500 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  804000 cP
@Shear Rate 500 1/s,
Temperature 200 °C		 804000 cP
@Shear Rate 500 1/s,
Temperature 392 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.021 cm/cm 0.021 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Melt Flow   1.9 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 1.9 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  2.4 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 2.4 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  92 92 ISO 2039-2
Hardness, Rockwell R  120 120 ISO 2039-2
Tensile Stress   10.0 MPa
@Strain 1.00 %,
Temperature 90.0 °C		 1450 psi
@Strain 1.00 %,
Temperature 194 °F		 ISO 11403-1 -2
  27.0 MPa
@Strain 4.20 %,
Temperature 90.0 °C		 3920 psi
@Strain 4.20 %,
Temperature 194 °F		 ISO 11403-1 -2
  32.5 MPa
@Strain 7.30 %,
Temperature 90.0 °C		 4710 psi
@Strain 7.30 %,
Temperature 194 °F		 ISO 11403-1 -2
  33.4 MPa
@Strain 10.4 %,
Temperature 90.0 °C		 4840 psi
@Strain 10.4 %,
Temperature 194 °F		 ISO 11403-1 -2
  33.9 MPa
@Strain 1.40 %,
Temperature 23.0 °C		 4920 psi
@Strain 1.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  35.9 MPa
@Strain 1.90 %,
Temperature 40.0 °C		 5210 psi
@Strain 1.90 %,
Temperature 104 °F		 ISO 11403-1 -2
  50.1 MPa
@Strain 2.20 %,
Temperature 0.000 °C		 7270 psi
@Strain 2.20 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  55.0 MPa
@Strain 2.10 %,
Temperature -40.0 °C		 7980 psi
@Strain 2.10 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  57.1 MPa
@Strain 7.70 %,
Temperature 40.0 °C		 8280 psi
@Strain 7.70 %,
Temperature 104 °F		 ISO 11403-1 -2
  59.8 MPa
@Strain 2.60 %,
Temperature -20.0 °C		 8670 psi
@Strain 2.60 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  60.1 MPa
@Strain 13.4 %,
Temperature 40.0 °C		 8720 psi
@Strain 13.4 %,
Temperature 104 °F		 ISO 11403-1 -2
  60.8 MPa
@Strain 5.40 %,
Temperature 23.0 °C		 8820 psi
@Strain 5.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  66.0 MPa
@Strain 9.50 %,
Temperature 23.0 °C		 9570 psi
@Strain 9.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  67.3 MPa
@Strain 13.6 %,
Temperature 23.0 °C		 9760 psi
@Strain 13.6 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  73.2 MPa
@Strain 8.80 %,
Temperature 0.000 °C		 10600 psi
@Strain 8.80 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  76.1 MPa
@Strain 15.4 %,
Temperature 0.000 °C		 11000 psi
@Strain 15.4 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  77.1 MPa
@Strain 21.4 %,
Temperature 0.000 °C		 11200 psi
@Strain 21.4 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  81.4 MPa
@Strain 10.4 %,
Temperature -20.0 °C		 11800 psi
@Strain 10.4 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  84.5 MPa
@Strain 18.2 %,
Temperature -20.0 °C		 12300 psi
@Strain 18.2 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  85.3 MPa
@Strain 26.0 %,
Temperature -20.0 °C		 12400 psi
@Strain 26.0 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  96.0 MPa
@Strain 12.6 %,
Temperature -40.0 °C		 13900 psi
@Strain 12.6 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  97.9 MPa
@Strain 25.1 %,
Temperature -40.0 °C		 14200 psi
@Strain 25.1 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  98.8 MPa
@Strain 37.7 %,
Temperature -40.0 °C		 14300 psi
@Strain 37.7 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  70.0 MPa 10200 psi ISO 527-1/-2
Elongation at Break  45 % 45 % Nominal; ISO 527-1/-2
Elongation at Yield  23 % 23 % ISO 527-1/-2
Tensile Modulus  3.00 GPa 435 ksi ISO 527-1/-2
Flexural Modulus  2.70 GPa 392 ksi ISO 178
Shear Modulus   0.2165 GPa
@Temperature 120 °C		 31.40 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.4832 GPa
@Temperature 70.0 °C		 70.08 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  0.8266 GPa
@Temperature 20.0 °C		 119.9 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  0.980 GPa
@Temperature -20.0 °C		 142 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.1339 GPa
@Temperature -50.0 °C		 164.46 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   0.31978 GPa
@Strain 9.10 %,
Temperature 100 °C		 46.381 ksi
@Strain 9.10 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.336 GPa
@Strain 29.3 %,
Temperature -40.0 °C		 48.7 ksi
@Strain 29.3 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  0.37551 GPa
@Strain 9.80 %,
Temperature 80.0 °C		 54.464 ksi
@Strain 9.80 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.392 GPa
@Strain 15.4 %,
Temperature 40.0 °C		 56.8 ksi
@Strain 15.4 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.408 GPa
@Strain 20.8 %,
Temperature -20.0 °C		 59.2 ksi
@Strain 20.8 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  0.435 GPa
@Strain 17.6 %,
Temperature 0.000 °C		 63.0 ksi
@Strain 17.6 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.520 GPa
@Strain 4.50 %,
Temperature 100 °C		 75.4 ksi
@Strain 4.50 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.611 GPa
@Strain 10.9 %,
Temperature 23.0 °C		 88.6 ksi
@Strain 10.9 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.639 GPa
@Strain 4.90 %,
Temperature 80.0 °C		 92.6 ksi
@Strain 4.90 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.742 GPa
@Strain 7.70 %,
Temperature 40.0 °C		 108 ksi
@Strain 7.70 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.762 GPa
@Strain 12.6 %,
Temperature -40.0 °C		 111 ksi
@Strain 12.6 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  0.783 GPa
@Strain 10.4 %,
Temperature -20.0 °C		 114 ksi
@Strain 10.4 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  0.827 GPa
@Strain 1.10 %,
Temperature 100 °C		 120 ksi
@Strain 1.10 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.832 GPa
@Strain 8.80 %,
Temperature 0.000 °C		 121 ksi
@Strain 8.80 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.05 GPa
@Strain 1.20 %,
Temperature 80.0 °C		 152 ksi
@Strain 1.20 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.13 GPa
@Strain 5.40 %,
Temperature 23.0 °C		 163 ksi
@Strain 5.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.89 GPa
@Strain 1.90 %,
Temperature 40.0 °C		 274 ksi
@Strain 1.90 %,
Temperature 104 °F		 ISO 11403-1 -2
  2.28 GPa
@Strain 2.20 %,
Temperature 0.000 °C		 330 ksi
@Strain 2.20 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.30 GPa
@Strain 2.60 %,
Temperature -20.0 °C		 334 ksi
@Strain 2.60 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.42 GPa
@Strain 1.40 %,
Temperature 23.0 °C		 351 ksi
@Strain 1.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.62 GPa
@Strain 2.10 %,
Temperature -40.0 °C		 380 ksi
@Strain 2.10 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  13.0 kJ/m² 6.19 ft-lb/in² ISO 180/1A
  11.0 kJ/m²
@Temperature -40.0 °C		 5.23 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Charpy Impact Unnotched  40.0 J/cm² 190 ft-lb/in² ISO 179/1eU
  35.0 J/cm²
@Temperature -30.0 °C		 167 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  1.50 J/cm² 7.14 ft-lb/in² ISO 179/1eA
  1.10 J/cm²
@Temperature -30.0 °C		 5.23 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+13 ohm-cm 1.00e+13 ohm-cm IEC 60093
Dielectric Constant   3.4
@Frequency 1.00e+6 Hz		 3.4
@Frequency 1.00e+6 Hz		 IEC 60250
  3.5
@Frequency 100 Hz		 3.5
@Frequency 100 Hz		 IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  160 °C 320 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  93.0 °C 199 °F ISO 75-1/-2
Vicat Softening Point  160 °C 320 °F 50°C/h 50N; ISO 306
Flammability, UL94  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >POM< ISO 11469
Processing Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM ISO 1043
Special characteristics Light stabilised or stable to light  
  U.V. stabilised or stable to weather  
UL recognition UL  

 

概述

pom（聚甲醛）

聚甲醛(英文：polyformaldehyde)热塑性结晶聚合物。被誉为“超钢”或者“赛钢”，又称聚氧亚甲基。英文缩写为POM。通常甲醛聚合所得之聚合物，聚合度不高，且易受热解聚。可用作有机化工、合成树脂的原料，也用作药物熏蒸剂。白色可燃结晶粉末，具有甲醛气味。 缓慢溶于冷水，在热水中溶解较快。

一般性能

聚甲醛是一种表面光滑、有光泽的硬而致密的材料，淡黄或白色，薄壁部分呈半透明。燃烧特性为容易燃烧，离火后继续燃烧，火焰上端呈黄色，下端呈蓝色，发生熔融滴落，有强烈的刺激性甲醛味、鱼腥臭。聚甲醛为白色粉末，一般不透明，着色性好，

力学性能

POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。POM的冲击强度较高,POM的摩擦因数小，耐磨性好。POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。

电学性能

POM的电绝缘性较好，几乎不受温度和湿度的影响；介电常数和介电损耗在很宽的温度、湿度和频率范围内变化很小；耐电弧性极好，并可在高温下保持。POM的介电强度与厚度有关，厚度0.127mm时为82.7kV/mm，厚度为1.88mm时为23.6kV/mm。

环境性能

POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。

POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。

成形性

结晶料，熔融范围窄，熔融和凝固快，料温稍低于熔融温度即发生结晶，流动性中等，吸湿小，可不经干燥处理。

优缺点

优点

1、具高机械强度和刚性；2、最高的疲劳强度；3、环境抵抗性、耐有机溶剂性佳；

4、耐反覆冲击性强；5、广泛的使用温度范围(-40℃~120℃)；6、良好的电气性质；

7、复原性良好；8、具自已润滑性、耐磨性良好；9、尺寸安定性优。

缺点

受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。

用途

多聚甲醛为高甲醛含量的固态甲醛，呈固体颗粒状、便于贮存和运输。在较高的温度下能变成甲醛蒸气，易于代替高浓度甲醛参与各种反应，有利于化工、制药等化学合成及其他工业领域的应用，特别是在要求使用无水甲醛作原料的合成方面，用途广泛。主要有以下几方面（1）农药：合成乙草胺、丁草胺和草甘膦等；（2）涂料：合成高档汽车用漆；（3）树脂：合成脲醛树脂、酚醛树脂、聚缩醛树脂、蜜胺树脂、离子交换树脂等及各种粘合剂；（4）造纸：合成纸张增强剂； （5）铸造：翻砂脱膜剂、合成铸造粘合剂；（6）养殖业：薰蒸消毒剂。（7）有机原料：用于制备季戊四醇、三羟甲基丙烷、甘油、丙烯酸、丙烯酸甲酯、甲基丙烯酸、N－羟基甲基丙烯酰胺、烷基苯酚、甲基乙烯基酮等。（8）其他：医药及消毒。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40617.html

免责声明: 本文 抗紫外线 耐老化 POM 美国杜邦 127UV NC010 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4