| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.965 g/cc | 0.0349 lb/in³ | ASTM D1505 | ||
| Viscosity Measurement | 0.70 @Temperature 30.0 °C |
0.70 @Temperature 86.0 °F |
Inherent, 0.25 g/100mL toluene | ||
| Vinyl Acetate Content | 40 % | 40 % | DuPont Method | ||
| Melt Index of Compound | 52 g/10 min | 52 g/10 min | ASTM D1238, modified | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 | 40 | 10 seconds, Shore A-2; ASTM D2240 | ||
| Tensile Strength at Break | 4.80 - 6.20 MPa | 696 - 899 psi | Samples die cut from pressed films, gage dimensions 2.23cm x 0.47cm x 0.13cm, crosshead speed 2in/min; ASTM D1708 | ||
| Elongation at Break | 1000 - 1300 % | 1000 - 1300 % | Samples die cut from pressed films, gage dimensions 2.23cm x 0.47cm x 0.13cm, crosshead speed 2in/min; ASTM D1708 | ||
| Tensile Modulus | 0.00300 GPa | 0.435 ksi | Samples die cut from pressed films, gage dimensions 2.23cm x 0.47cm x 0.13cm, crosshead speed 2in/min; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Ring & Ball Softening Point | 104 °C | 219 °F | ASTM E28 | ||
| De |
|||||
| Antioxidant | 550 ppm | BHT | |||
| Odor | Slight | ||||
| Residual VA Monomer, wt% | <0.3 | ||||
| Vinyl Acetate Content | 40 wt.% | DuPont Method | |||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com