| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 4.2 % | 4.2 % | ExxonMobil Method | ||
| Melt Flow | 1.25 g/10 min | 1.25 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 4000 ppm | 4000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.07 MPa | 1170 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.65 MPa | 1110 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 | ||
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 7.0 % | 7.0 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.5 % | 5.5 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 170 g | 170 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 90 g | 90 g | ASTM D1922 | ||
| Dart dro Test | 180 g | 0.397 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.3 MPa | 3530 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 23.2 MPa | 3360 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 141 MPa | 20400 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 163 MPa | 23700 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 104 °C | 220 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 91.0 °C | 196 °F | ExxonMobil Method | ||
| Vicat Softening Point | 87.2 °C | 189 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.4 % | 7.4 % | ASTM D1003 | ||
| Gloss | 68 % | 68 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified | ||
| De |
|||||
| Features | Thermal Stabilizer | ||||
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com