聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），20%的玻璃纤维填充
LCP E115i 材料说明：
15%玻璃增强
LCP E115i 填料/增强材料：
玻璃纤维增强材料, 15% 填料按重量
LCP E115i 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | -0.00200 cm/cm | -0.00200 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 43.0 | 43.0 | ISO 2039-2 |
| Tensile Strength at Break | 175 MPa | 25400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.30 % | 2.30 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | ISO 180/1A |
| 101 kJ/m² @Temperature 23.0 °C |
48.1 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.94 @Frequency 2.05e+9 Hz |
3.94 @Frequency 2.05e+9 Hz |
|
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Dissipation Factor | 50.0 @Frequency 2.05e+9 Hz |
50.0 @Frequency 2.05e+9 Hz |
|
| Thermal Properties | Metric | English | Comments |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 298 °C | 568 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ISO 75-1, -2 |
| Vicat Softening Point | 202 °C | 396 °F | ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|