物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183-1 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | b.o. ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | b.o. ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 50 % | >= 50 % | Nominal, 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² @Temperature -20.0 °C |
21.4 ft-lb/in² @Temperature -4.00 °F |
ISO 180-A |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-A | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 100 V | 100 V | CTI M; Solution B; IEC 60112 |
| 225 V | 225 V | Solution A; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1,-2 |
| Vicat Softening Point | 122 °C @Load 5.10 kg |
252 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| Shrinkage | 0.10 - 0.20 % | 0.10 - 0.20 % | post-shrinkage; b.o. ISO 2577 |
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com