聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），矿物填充
LCP E531i 材质说明：
低翘曲、易流动、表面光滑的矿物填充级。
LCP E531i 加工方法：
注塑成型
LCP E531i 的物性表:：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.645 g/cc | 0.05943 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000 cm/cm | 0.000 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 4.00 % | 4.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1, -2 |