聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），40%的玻璃纤维填充
LCP E845i 材料说明：
LDS LCP高DTUL和影响能力
LCP E845i 加工方法：
注塑成型
LCP E845i 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000 cm/cm | 0.000 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00230 cm/cm | 0.00230 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.70 % | 1.70 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.87 @Frequency 1.00e+6 Hz |
3.87 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.35 @Frequency 2.05e+9 Hz |
4.35 @Frequency 2.05e+9 Hz |
||
| Dissipation Factor | 0.0370 @Frequency 1.00e+6 Hz |
0.0370 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 50.0 @Frequency 2.05e+9 Hz |
50.0 @Frequency 2.05e+9 Hz |
||
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C | 4.44 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C | 32.2 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-1, -2 |