| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C; 50% RH | ||
| Viscosity Measurement | 160 | 160 | [ml/g]; Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | Sheet; ISO 294 | ||
| Linear Mold Shrinkage, Transverse | 0.022 cm/cm | 0.022 in/in | Sheet; ISO 294 | ||
| Melt Flow | 11.7 g/10 min @Load 2.16 kg, Temperature 250 °C |
11.7 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527-2 | ||
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Break | >= 3.5 % | >= 3.5 % | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-2 | ||
| >= 50 % | >= 50 % | 50 mm/min; ISO 527-2 | |||
| Modulus of Elasticity | 2.60 GPa | 377 ksi | ISO 527-2 | ||
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 | ||
| Charpy Impact Unnotched | 22.0 J/cm² @Temperature -30.0 °C |
105 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 5.00e+15 ohm-cm | 5.00e+15 ohm-cm | IEC 93 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 93 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 250 | ||
| 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
IEC 250 | |||
| Dielectric Strength | 39.0 kV/mm | 991 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0019 @Frequency 100 Hz |
0.0019 @Frequency 100 Hz |
IEC 250 | ||
| 0.0219 @Frequency 1.00e+6 Hz |
0.0219 @Frequency 1.00e+6 Hz |
IEC 250 | |||
| Comparative Tracking Index | 475 V | 475 V | Test solution A; IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 9.00 - 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
5.00 - 8.33 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Diameter 0.400 mm |
HB @Diameter 0.0157 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | for shrinkage test | ||
| 250 - 270 °C | 482 - 518 °F | Pipe extrusion | |||
| 250 - 270 °C | 482 - 518 °F | Semi-finished extrusion | |||
| 260 - 270 °C | 500 - 518 °F | Injection-molding | |||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection molding | ||
| 60.0 °C | 140 °F | for shrinkage test | |||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350 °C | ASTM D1929 | |||
| Primary Processing Technique | Coating and Injection Molding | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com