LCP FIT70 材料说明：35%玻璃和矿物增强级。它提供了良好的流动性，低翘曲，优良的表面外观，尺寸稳定性好，良好的熔接强度。
LCP FIT70 加工方法：注塑成型
LCP FIT70 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000500 cm/cm | 0.000500 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00430 cm/cm | 0.00430 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 110 MPa | 16000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.60 % | 2.60 % | flexural; ISO 178 |
| 2.60 % | 2.60 % | 5mm/min; ISO 527-2/1A | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 6.00e+15 ohm | 6.00e+15 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C | 4.44 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C | 23.9 µin/in-°F | ISO 11359-2 |
| Melting Point | 331 °C | 628 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 278 °C | 532 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1, -2 |