LCP MT4350 材质说明：低翘曲、易流动、表面光滑的矿物填充级。
LCP MT4350 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000 cm/cm | 0.000 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 105 MPa | 15200 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.20 % | 3.20 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 9.80 GPa | 1420 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 125 MPa | 18100 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.20 kJ/m² | 2.47 ft-lb/in² | ISO 180/1A |
| 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.60 @Frequency 1.00e+6 Hz |
3.60 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 46.0 kV/mm | 1170 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0310 @Frequency 1.00e+6 Hz |
0.0310 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 11.0 µm/m-°C | 6.11 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 11.0 µm/m-°C | 6.11 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|