LCP MT1335 材料说明：最佳的高电流电弧点火（海）性能。玻璃/聚四氟乙烯填充。
LCP MT1335 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55.0 | 55.0 | ISO 2039-2 |
| Tensile Strength at Break | 171 MPa | 24800 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.30 % | 3.30 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 206 MPa | 29900 psi | ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Compressive Strength | 77.0 MPa @Strain 1.00 % |
11200 psi @Strain 1.00 % |
ISO 604 |
| Compressive Modulus | 10.5 GPa | 1520 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180/1A |
| 33.0 kJ/m² @Temperature 23.0 °C |
15.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 3.80 J/cm² | 18.1 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 2.60 J/cm² | 12.4 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.10 @Frequency 1.00e+6 Hz |
3.10 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.50 @Frequency 100 Hz |
3.50 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0160 @Frequency 1.00e+6 Hz |
0.0160 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0200 @Frequency 100 Hz |
0.0200 @Frequency 100 Hz |
IEC 60250 | |
| Arc Resistance | 130 sec | 130 sec | Internal |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 0.000 µm/m-°C | 0.000 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 19.0 µm/m-°C | 10.6 µin/in-°F | ISO 11359-2 |
| Melting Point | 280 °C | 536 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 162 °C | 324 °F | ISO 75-1, -2 |
| Vicat Softening Point | 146 °C | 295 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |