LCP S471 材料说明：高流动性，高耐热性，低翘曲，厚壁（大于0.2mm）或薄（＜0.2mm）和厚壁组合件。
LCP S471 加工方法：注塑成型
LCP S471 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.40 % | 1.40 % | 5mm/min; ISO 527-2/1A |
| 2.00 % | 2.00 % | flexural; ISO 178 | |
| Tensile Modulus | 12.0 GPa | 1740 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 |
| Dielectric Constant | 4.00 @Frequency 1.00e+6 Hz |
4.00 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.00700 @Frequency 1.00e+6 Hz |
0.00700 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C | 4.44 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 17.0 µm/m-°C | 9.44 µin/in-°F | ISO 11359-2 |
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 271 °C | 520 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 | V-0 | |