LCP S475 材质说明：超高流动，高耐热性，低翘曲变形。
LCP S475 加工方法：注塑成型
LCP S475 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000 cm/cm | 0.000 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00370 cm/cm | 0.00370 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 135 MPa | 19600 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.80 % | 1.80 % | 5mm/min; ISO 527-2/1A |
| 2.40 % | 2.40 % | flexural; ISO 178 | |
| Tensile Modulus | 12.3 GPa | 1780 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 1.45 J/cm² | 6.90 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.70 @Frequency 1.00e+6 Hz |
3.70 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.95 @Frequency 2.05e+9 Hz |
3.95 @Frequency 2.05e+9 Hz |
||
| Dissipation Factor | 0.00800 @Frequency 1.00e+6 Hz |
0.00800 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 10.0 @Frequency 2.05e+9 Hz |
10.0 @Frequency 2.05e+9 Hz |
||
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-2 |
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 305 °C | 581 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 213 °C | 415 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 | V-0 | |