  4. 杜邦高性能聚合物LW9020FR NC010PBT+ ASA

杜邦高性能聚合物LW9020FR NC010PBT+ ASA

杜邦高性能聚合物Crastin ®LW9020FR NC010 PBT+ ASA 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT）；PBT + ASA共混，玻璃纤维增强 材料说明：低翘曲的特点增强阻燃聚对苯二甲酸丁二醇酯共混物20%玻璃 Crastin LW9020FR NC010是20%玻璃纤维增强阻燃聚对苯二甲酸丁二醇酯共混物注射成型
 物性表：

 
Physical Properties Metric English Comments
Density  1.36 g/cc 0.0491 lb/in³  
  1.52 g/cc 0.0549 lb/in³ ISO 1183
Water Absorption  0.78 %
@Thickness 2.00 mm		 0.78 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.230 %
@Thickness 2.00 mm		 0.230 %
@Thickness 0.0787 in		 Sim. to ISO 62
Linear Mold Shrinkage, Flow  0.0040 cm/cm 0.0040 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0080 cm/cm 0.0080 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  110 MPa 16000 psi ISO 527-1/-2
Tensile Stress   16.22 MPa
@Strain 0.260 %,
Temperature 40.0 °C		 2353 psi
@Strain 0.260 %,
Temperature 104 °F		 ISO 11403-1 -2
  17.6 MPa
@Strain 0.400 %,
Temperature 90.0 °C		 2550 psi
@Strain 0.400 %,
Temperature 194 °F		 ISO 11403-1 -2
  43.3 MPa
@Strain 0.580 %,
Temperature 23.0 °C		 6280 psi
@Strain 0.580 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  46.1 MPa
@Strain 1.62 %,
Temperature 90.0 °C		 6690 psi
@Strain 1.62 %,
Temperature 194 °F		 ISO 11403-1 -2
  53.1 MPa
@Strain 2.80 %,
Temperature 90.0 °C		 7700 psi
@Strain 2.80 %,
Temperature 194 °F		 ISO 11403-1 -2
  55.58 MPa
@Strain 0.980 %,
Temperature 40.0 °C		 8061 psi
@Strain 0.980 %,
Temperature 104 °F		 ISO 11403-1 -2
  76.95 MPa
@Strain 1.14 %,
Temperature 23.0 °C		 11160 psi
@Strain 1.14 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  78.69 MPa
@Strain 1.71 %,
Temperature 40.0 °C		 11410 psi
@Strain 1.71 %,
Temperature 104 °F		 ISO 11403-1 -2
  97.03 MPa
@Strain 1.71 %,
Temperature 23.0 °C		 14070 psi
@Strain 1.71 %,
Temperature 73.4 °F		 ISO 11403-1 -2
Elongation at Break  2.0 % 2.0 % ISO 527-1/-2
Tensile Modulus  8.50 GPa 1230 ksi ISO 527-1/-2
Flexural Strength  155 MPa 22500 psi ISO 178
Secant Modulus   4.29 GPa
@Strain 1.93 %,
Temperature 40.0 °C		 622 ksi
@Strain 1.93 %,
Temperature 104 °F		 ISO 11403-1 -2
  5.30 GPa
@Strain 1.91 %,
Temperature 23.0 °C		 769 ksi
@Strain 1.91 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  5.67 GPa
@Strain 0.980 %,
Temperature 40.0 °C		 823 ksi
@Strain 0.980 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.24 GPa
@Strain 0.260 %,
Temperature 40.0 °C		 905 ksi
@Strain 0.260 %,
Temperature 104 °F		 ISO 11403-1 -2
  6.75 GPa
@Strain 1.14 %,
Temperature 23.0 °C		 979 ksi
@Strain 1.14 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  7.47 GPa
@Strain 0.580 %,
Temperature 23.0 °C		 1080 ksi
@Strain 0.580 %,
Temperature 73.4 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  6.00 kJ/m² 2.86 ft-lb/in² ISO 180/1A
  6.00 kJ/m²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  33.0 kJ/m² 15.7 ft-lb/in² ISO 180/1U
  33.0 kJ/m²
@Temperature -30.0 °C		 15.7 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  4.00 J/cm² 19.0 ft-lb/in² ISO 179/1eU
  3.50 J/cm²
@Temperature -30.0 °C		 16.7 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.700 J/cm² 3.33 ft-lb/in² ISO 179/1eA
  0.650 J/cm²
@Temperature -30.0 °C		 3.09 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  7500 MPa
@Time 3600 sec		 1.09e+6 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  6000 MPa
@Time 3.60e+6 sec		 870000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+14 ohm 1.00e+14 ohm IEC 60093
Dielectric Constant   3.5
@Frequency 1.00e+6 Hz		 3.5
@Frequency 1.00e+6 Hz		 IEC 60250
  3.7
@Frequency 100 Hz		 3.7
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  29.0 kV/mm 737 kV/in IEC 60243-1
  20.0 kV/mm
@Thickness 2.00 mm		 508 kV/in
@Thickness 0.0787 in		 Short Time; IEC 60243-1
  20.0 kV/mm
@Thickness 2.00 mm		 508 kV/in
@Thickness 0.0787 in		 20s; IEC 60243-1
  29.0 kV/mm
@Thickness 1.00 mm		 737 kV/in
@Thickness 0.0394 in		 Short Time; IEC 60243-1
Dissipation Factor   0.0030
@Frequency 100 Hz		 0.0030
@Frequency 100 Hz		 ASTM D150
  0.0030
@Frequency 100 Hz		 0.0030
@Frequency 100 Hz		 IEC 60250
  0.015
@Frequency 1.00e+6 Hz		 0.015
@Frequency 1.00e+6 Hz		 IEC 60250
  0.015
@Frequency 1.00e+6 Hz		 0.015
@Frequency 1.00e+6 Hz		 ASTM D150
Comparative Tracking Index  300 V 300 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  30.0 µm/m-°C 16.7 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C 55.6 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.90 J/g-°C 0.454 BTU/lb-°F  
Thermal Conductivity  0.250 W/m-K 1.74 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  215 °C 419 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  175 °C 347 °F ISO 75-1/-2
Flammability, UL94  V-0
@Thickness 1.50 mm		 V-0
@Thickness 0.0591 in		 IEC 60695-11-10
Oxygen Index  27 % 27 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT+ASA-GF20FR(17)< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT+ASA-GF20FR(17)  
UL recognition UL

图：


上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40864.html

免责声明: 本文 杜邦高性能聚合物LW9020FR NC010PBT+ ASA 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4