  4. 杜邦高性能聚合物s600f10 NC010/高粘度

杜邦高性能聚合物s600f10 NC010/高粘度

杜邦高性能聚合物Crastin®s600f10 NC010聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT） 材料说明：无筋高粘度聚对苯二甲酸乙二醇酯用于挤出和注塑成型 Crastin s600f10 NC010是一种无筋润滑中高粘度聚对苯二甲酸乙二醇酯树脂注塑成型。
 物性表：

 
Physical Properties Metric English Comments
Density  1.11 g/cc 0.0401 lb/in³  
  1.30 g/cc 0.0470 lb/in³ ISO 1183
Water Absorption  0.50 %
@Thickness 2.00 mm		 0.50 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   116000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 116000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  148000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 148000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  194000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 194000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  279000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 279000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  369000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 369000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  496000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 496000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.017 cm/cm 0.017 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.016 cm/cm 0.016 in/in ISO 294-4 2577
Melt Flow  10.1 g/10 min
@Load 2.16 kg,
Temperature 250 °C		 10.1 g/10 min
@Load 4.76 lb,
Temperature 482 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   5.910 MPa
@Strain 3.58031 %,
Temperature 150 °C		 857.1 psi
@Strain 3.58031 %,
Temperature 302 °F		 ISO 11403-1 -2
  10.46 MPa
@Strain 2.84 %,
Temperature 90.0 °C		 1517 psi
@Strain 2.84 %,
Temperature 194 °F		 ISO 11403-1 -2
  12.81 MPa
@Strain 14.3213 %,
Temperature 150 °C		 1858 psi
@Strain 14.3213 %,
Temperature 302 °F		 ISO 11403-1 -2
  14.44 MPa
@Strain 25.0622 %,
Temperature 150 °C		 2095 psi
@Strain 25.0622 %,
Temperature 302 °F		 ISO 11403-1 -2
  19.98 MPa
@Strain 1.85 %,
Temperature 40.0 °C		 2898 psi
@Strain 1.85 %,
Temperature 104 °F		 ISO 11403-1 -2
  20.87 MPa
@Strain 9.55 %,
Temperature 90.0 °C		 3027 psi
@Strain 9.55 %,
Temperature 194 °F		 ISO 11403-1 -2
  23.459 MPa
@Strain 0.768184 %,
Temperature -40.0 °C		 3402.4 psi
@Strain 0.768184 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  23.89 MPa
@Strain 16.78 %,
Temperature 90.0 °C		 3465 psi
@Strain 16.78 %,
Temperature 194 °F		 ISO 11403-1 -2
  24.579 MPa
@Strain 0.8588 %,
Temperature 0.000 °C		 3564.9 psi
@Strain 0.8588 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  24.63 MPa
@Strain 23.49 %,
Temperature 90.0 °C		 3572 psi
@Strain 23.49 %,
Temperature 194 °F		 ISO 11403-1 -2
  31.6 MPa
@Strain 1.33 %,
Temperature 23.0 °C		 4580 psi
@Strain 1.33 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  35.26 MPa
@Strain 7.41 %,
Temperature 40.0 °C		 5114 psi
@Strain 7.41 %,
Temperature 104 °F		 ISO 11403-1 -2
  39.33 MPa
@Strain 12.94 %,
Temperature 40.0 °C		 5704 psi
@Strain 12.94 %,
Temperature 104 °F		 ISO 11403-1 -2
  40.12 MPa
@Strain 18.47 %,
Temperature 40.0 °C		 5819 psi
@Strain 18.47 %,
Temperature 104 °F		 ISO 11403-1 -2
  49.3 MPa
@Strain 2.28 %,
Temperature 23.0 °C		 7150 psi
@Strain 2.28 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  54.0 MPa
@Strain 3.23 %,
Temperature 23.0 °C		 7830 psi
@Strain 3.23 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  54.50 MPa
@Strain 2.147 %,
Temperature 0.000 °C		 7905 psi
@Strain 2.147 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  69.28 MPa
@Strain 3.4352 %,
Temperature 0.000 °C		 10050 psi
@Strain 3.4352 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  74.71 MPa
@Strain 3.07274 %,
Temperature -40.0 °C		 10840 psi
@Strain 3.07274 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  93.67 MPa
@Strain 5.37729 %,
Temperature -40.0 °C		 13590 psi
@Strain 5.37729 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  5.00 MPa
@Strain 0.220 %,
Time 360000 sec		 725 psi
@Strain 0.220 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.195 %,
Time 3600 sec		 725 psi
@Strain 0.195 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.280 %,
Time 3.60e+6 sec		 725 psi
@Strain 0.280 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.397 %,
Time 3.60e+7 sec		 725 psi
@Strain 0.397 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.202 %,
Time 36000 sec		 725 psi
@Strain 0.202 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 2.61 %,
Time 3.60e+7 sec		 2900 psi
@Strain 2.61 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.820 %,
Time 3600 sec		 2900 psi
@Strain 0.820 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  25.0 MPa
@Strain 2.03 %,
Time 3.60e+6 sec		 3630 psi
@Strain 2.03 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  25.0 MPa
@Strain 1.34 %,
Time 360000 sec		 3630 psi
@Strain 1.34 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  25.0 MPa
@Strain 1.17 %,
Time 36000 sec		 3630 psi
@Strain 1.17 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
Tensile Strength, Yield  57.0 MPa 8270 psi ISO 527-1/-2
Elongation at Break  >= 50 % >= 50 % Nominal; ISO 527-1/-2
Elongation at Yield  4.0 % 4.0 % ISO 527-1/-2
Tensile Modulus  2.60 GPa 377 ksi ISO 527-1/-2
Flexural Strength  85.0 MPa 12300 psi ISO 178
Flexural Modulus  2.30 GPa 334 ksi ISO 178
Shear Modulus   0.0640 GPa
@Temperature 160 °C		 9.28 ksi
@Temperature 320 °F		 Dynamic; ISO 11403-1 -2
  0.0900 GPa
@Temperature 120 °C		 13.1 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.187 GPa
@Temperature 70.0 °C		 27.1 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  0.869 GPa
@Temperature 20.0 °C		 126 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  0.959 GPa
@Temperature -20.0 °C		 139 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.07 GPa
@Temperature -50.0 °C		 155 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus   0.094872 GPa
@Strain 22.0028 %,
Temperature 100 °C		 13.760 ksi
@Strain 22.0028 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.164 GPa
@Strain 11.0014 %,
Temperature 100 °C		 23.8 ksi
@Strain 11.0014 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.270 GPa
@Strain 14.77 %,
Temperature 40.0 °C		 39.1 ksi
@Strain 14.77 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.30625 GPa
@Strain 2.72 %,
Temperature 100 °C		 44.418 ksi
@Strain 2.72 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.476 GPa
@Strain 7.41 %,
Temperature 40.0 °C		 69.0 ksi
@Strain 7.41 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.08 GPa
@Strain 1.85 %,
Temperature 40.0 °C		 157 ksi
@Strain 1.85 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.55 GPa
@Strain 6.14547 %,
Temperature -40.0 °C		 225 ksi
@Strain 6.14547 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.82 GPa
@Strain 3.8646 %,
Temperature 0.000 °C		 265 ksi
@Strain 3.8646 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.16 GPa
@Strain 2.28 %,
Temperature 23.0 °C		 314 ksi
@Strain 2.28 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.38 GPa
@Strain 1.33 %,
Temperature 23.0 °C		 345 ksi
@Strain 1.33 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.43 GPa
@Strain 3.07274 %,
Temperature -40.0 °C		 353 ksi
@Strain 3.07274 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.54 GPa
@Strain 2.147 %,
Temperature 0.000 °C		 368 ksi
@Strain 2.147 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.86 GPa
@Strain 0.8588 %,
Temperature 0.000 °C		 415 ksi
@Strain 0.8588 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.05 GPa
@Strain 0.768184 %,
Temperature -40.0 °C		 443 ksi
@Strain 0.768184 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  5.00 kJ/m² 2.38 ft-lb/in² ISO 180/1A
  5.00 kJ/m²
@Temperature -30.0 °C		 2.38 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  NB NB ISO 180/1U
  130 kJ/m²
@Temperature -30.0 °C		 61.9 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.500 J/cm² 2.38 ft-lb/in² ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   200 MPa
@Pressure 10.0 MPa,
Temperature 110 °C		 29000 psi
@Pressure 1450 psi,
Temperature 230 °F		 ISO 11403-1 -2
  217.95 MPa
@Pressure 8.00 MPa,
Temperature 110 °C		 31611 psi
@Pressure 1160 psi,
Temperature 230 °F		 ISO 11403-1 -2
  244.65 MPa
@Pressure 6.00 MPa,
Temperature 110 °C		 35484 psi
@Pressure 870 psi,
Temperature 230 °F		 ISO 11403-1 -2
  275 MPa
@Pressure 4.00 MPa,
Temperature 110 °C		 39900 psi
@Pressure 580 psi,
Temperature 230 °F		 ISO 11403-1 -2
  298 MPa
@Pressure 2.00 MPa,
Temperature 110 °C		 43300 psi
@Pressure 290 psi,
Temperature 230 °F		 ISO 11403-1 -2
  340 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 49300 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  350 MPa
@Pressure 14.0 MPa,
Temperature 60.0 °C		 50800 psi
@Pressure 2030 psi,
Temperature 140 °F		 ISO 11403-1 -2
  376 MPa
@Pressure 12.0 MPa,
Temperature 60.0 °C		 54600 psi
@Pressure 1740 psi,
Temperature 140 °F		 ISO 11403-1 -2
  407 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 59000 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  439.56 MPa
@Pressure 8.00 MPa,
Temperature 60.0 °C		 63753 psi
@Pressure 1160 psi,
Temperature 140 °F		 ISO 11403-1 -2
  476.19 MPa
@Pressure 6.00 MPa,
Temperature 60.0 °C		 69066 psi
@Pressure 870 psi,
Temperature 140 °F		 ISO 11403-1 -2
  517 MPa
@Pressure 4.00 MPa,
Temperature 60.0 °C		 75100 psi
@Pressure 580 psi,
Temperature 140 °F		 ISO 11403-1 -2
  560 MPa
@Pressure 2.00 MPa,
Temperature 60.0 °C		 81300 psi
@Pressure 290 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2010 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 292000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2310 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 336000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2440 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 354000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2500 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 363000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2530 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 367000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2564.1 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 371890 psi
@Pressure 725 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2600 MPa
@Time 3600 sec		 377000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  160 MPa
@Pressure 10.0 MPa,
Temperature 110 °C		 23200 psi
@Pressure 1450 psi,
Temperature 230 °F		 ISO 11403-1 -2
  177 MPa
@Pressure 8.00 MPa,
Temperature 110 °C		 25700 psi
@Pressure 1160 psi,
Temperature 230 °F		 ISO 11403-1 -2
  204 MPa
@Pressure 6.00 MPa,
Temperature 110 °C		 29600 psi
@Pressure 870 psi,
Temperature 230 °F		 ISO 11403-1 -2
  236 MPa
@Pressure 4.00 MPa,
Temperature 110 °C		 34300 psi
@Pressure 580 psi,
Temperature 230 °F		 ISO 11403-1 -2
  262 MPa
@Pressure 2.00 MPa,
Temperature 110 °C		 38000 psi
@Pressure 290 psi,
Temperature 230 °F		 ISO 11403-1 -2
  270 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 39100 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  281 MPa
@Pressure 14.0 MPa,
Temperature 60.0 °C		 40800 psi
@Pressure 2030 psi,
Temperature 140 °F		 ISO 11403-1 -2
  307 MPa
@Pressure 12.0 MPa,
Temperature 60.0 °C		 44500 psi
@Pressure 1740 psi,
Temperature 140 °F		 ISO 11403-1 -2
  333 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 48300 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  352 MPa
@Pressure 8.00 MPa,
Temperature 60.0 °C		 51100 psi
@Pressure 1160 psi,
Temperature 140 °F		 ISO 11403-1 -2
  361 MPa
@Pressure 6.00 MPa,
Temperature 60.0 °C		 52400 psi
@Pressure 870 psi,
Temperature 140 °F		 ISO 11403-1 -2
  367 MPa
@Pressure 4.00 MPa,
Temperature 60.0 °C		 53200 psi
@Pressure 580 psi,
Temperature 140 °F		 ISO 11403-1 -2
  371 MPa
@Pressure 2.00 MPa,
Temperature 60.0 °C		 53700 psi
@Pressure 290 psi,
Temperature 140 °F		 ISO 11403-1 -2
  498 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 72300 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1230 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 179000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1390 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 202000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1450 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 210000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1709.4 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 247930 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1790 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 259000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1800 MPa
@Time 3.60e+6 sec		 261000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm IEC 60093
Dielectric Constant   3.2
@Frequency 1.00e+6 Hz		 3.2
@Frequency 1.00e+6 Hz		 IEC 60250
  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  26.0 kV/mm 660 kV/in IEC 60243-1
  15.0 kV/mm
@Thickness 2.00 mm		 381 kV/in
@Thickness 0.0787 in		 20s; IEC 60243-1
  26.0 kV/mm
@Thickness 1.00 mm		 660 kV/in
@Thickness 0.0394 in		 Short Time; IEC 60243-1
Dissipation Factor   0.0020
@Frequency 100 Hz		 0.0020
@Frequency 100 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  2.10 J/g-°C 0.502 BTU/lb-°F  
Thermal Conductivity  0.210 W/m-K 1.46 BTU-in/hr-ft²-°F of melt
Melting Point  223 °C 433 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  115 °C 239 °F ISO 75-1/-2
  180 °C 356 °F annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  50.0 °C 122 °F ISO 75-1/-2
  60.0 °C 140 °F annealed; ISO 75-1/-2
Vicat Softening Point  175 °C 347 °F 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  55.0 °C 131 °F 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Oxygen Index  22 % 22 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Emission of organic compounds 145 µgC/g VDA 277
Odour class 3 VDA 270
Part Marking Code >PBT< ISO 11469
Processing Coatable  
  Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT  
UL recognition UL

图：

 
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40881.html

免责声明: 本文 杜邦高性能聚合物s600f10 NC010/高粘度 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4