LCP 5130l 材料说明：泽尼特5130l是30%玻璃纤维增强高韧性LCP树脂
LCP 5130l 加工方法：注塑成型
LCP 5130l 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000500 cm/cm | 0.000500 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00730 cm/cm | 0.00730 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 145 MPa | 21000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.50 % | 3.50 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.0 GPa | 1450 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.30 @Frequency 1.00e+6 Hz |
3.30 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.07 @Frequency 2.05e+9 Hz |
4.07 @Frequency 2.05e+9 Hz |
||
| Dissipation Factor | 0.00800 @Frequency 1.00e+6 Hz |
0.00800 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 40.0 @Frequency 2.05e+9 Hz |
40.0 @Frequency 2.05e+9 Hz |
||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 320 °C | 608 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|