LCP ze88410nxl 材料说明：40%玻璃纤维增强，焊缝强度高，低翘曲及添加润滑性。
LCP ze88410nxl 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.00 % | 1.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 15.9 GPa | 2310 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 15.8 GPa | 2290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C | 6.67 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 82.0 µm/m-°C | 45.6 µin/in-°F | ISO 11359-2 |
| Melting Point | 328 °C | 622 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 263 °C | 505 °F | ISO 75-1, -2 |
| Vicat Softening Point | 239 °C | 462 °F | ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.250 mm |
V-0 @Thickness 0.00984 in |
|