LCP ze55205 材料说明：泽尼特«ze55205是黑色钢筋LCP树脂具有高介电常数。
LCP ze55205 加工方法：注塑成型
性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.89 g/cc | 0.0683 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 125 MPa | 18100 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.50 % | 2.50 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 14.26 GPa | 2068 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 12.165 GPa | 1764.4 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | ISO 180/1A |
| 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 3.60 J/cm² | 17.1 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.52 @Frequency 1.00e+6 Hz |
4.52 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 6.07 @Frequency 2.05e+9 Hz |
6.07 @Frequency 2.05e+9 Hz |
||
| Dissipation Factor | 0.0190 @Frequency 1.00e+6 Hz |
0.0190 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 40.0 @Frequency 2.05e+9 Hz |
40.0 @Frequency 2.05e+9 Hz |
||
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 276 °C | 529 °F | ISO 75-1, -2 |