150 LCP 材料说明：在提高蠕变抗力A130。可以减少与A130部分翘曲。50%玻璃增强。
150 LCP 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 93 | 93 | ISO 2039-2 |
| Tensile Strength at Break | 160 MPa | 23200 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.1 % | 1.1 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 22.0 GPa | 3190 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 21.0 GPa | 3050 ksi | ISO 178 |
| Compressive Strength | 140 MPa | 20300 psi | 1% strain; ISO 604 |
| Compressive Modulus | 21.0 GPa | 3050 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1 hour | 21300 MPa | 3.09e+6 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 18600 MPa | 2.70e+6 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.5 @Frequency 100 Hz |
4.5 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 @Frequency 100 Hz |
0.010 @Frequency 100 Hz |
IEC 60250 |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Arc Resistance | 180 sec | 180 sec | Internal |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 7.00 µm/m-°C | 3.89 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 19.0 µm/m-°C | 10.6 µin/in-°F | ISO 11359-2 |
| Melting Point | 280 °C | 536 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 203 °C | 397 °F | ISO 75-1, -2 |
| Vicat Softening Point | 177 °C | 351 °F | B50 (50°C/h 50N); ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |