| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ISO 294-4 | ||
| Melt Flow | 33.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
33.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
[cm3/10min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | ASTM D638 | ||
| 54.0 MPa | 7830 psi | 50mm/min; ISO 527-2/1A | |||
| Elongation at Break | 37.0 % | 37.0 % | |||
| 180 % | 180 % | ASTM D638 | |||
| Elongation at Yield | 3.90 % | 3.90 % | ASTM D638 | ||
| 8.00 % | 8.00 % | 50mm/min; ISO 527-2/1A | |||
| Tensile Modulus | 2.40 GPa | 348 ksi | 50mm/min; ISO 527-2/1A | ||
| Flexural Strength | 69.0 MPa | 10000 psi | ISO 178 | ||
| 82.7 MPa | 12000 psi | ASTM D790 | |||
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 | ||
| 2.48 GPa | 360 ksi | ASTM D790 | |||
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 4.60 kJ/m² @Temperature -30.0 °C |
2.19 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A | ||
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/1U | |||
| Charpy Impact Unnotched | 21.8 J/cm² | 104 ft-lb/in² | partial break; ISO 179/1eU | ||
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA | ||
| 0.450 J/cm² @Temperature -30.0 °C |
2.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| 1.20e+17 ohm-cm | 1.20e+17 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.33 @Frequency 1.00e+6 Hz |
3.33 @Frequency 1.00e+6 Hz |
ASTM D150 | ||
| 3.50 @Frequency 1.00e+6 Hz |
3.50 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| 3.70 @Frequency 100 Hz |
3.70 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 15.4 kV/mm | 390 kV/in | short term; ASTM D149 | ||
| Dissipation Factor | 0.00300 @Frequency 100 Hz |
0.00300 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0210 @Frequency 1.00e+6 Hz |
0.0210 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| 0.0210 @Frequency 1.00e+6 Hz |
0.0210 @Frequency 1.00e+6 Hz |
ASTM D150 | |||
| Arc Resistance | 181 sec | 181 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ASTM D648 | ||
| 166 °C | 331 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1, -2 | ||
| 56.1 °C | 133 °F | ASTM D648 | |||
| Vicat Softening Point | 175 °C | 347 °F | ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 65.0 - 93.0 °C | 149 - 199 °F | cavity | ||
| 250 - 260 °C | 482 - 500 °F | hot runner | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 250 °C | 482 °F | ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.0200 % | <= 0.0200 % | |||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Processing conditions acc. ISO | 7792 | ||||
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com