LCP C130 材料说明：
LCP C130 加工方法：注塑成型
LCP C130 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | IEC 527 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | ISO 527 |
| Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 |
| Compressive Strength | 139 MPa | 20200 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 22.0 GPa | 3190 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179 |
| Tensile Impact Strength | 70.0 kJ/m² | 33.3 ft-lb/in² | Notched; ASTM D1822 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 |
| Dielectric Constant | 3.4 @Frequency 1e+7 Hz |
3.4 @Frequency 1e+7 Hz |
|
| 3.8 @Frequency 1000 Hz |
3.8 @Frequency 1000 Hz |
IEC 250 | |
| Dissipation Factor | 0.0090 @Frequency 1e+7 Hz |
0.0090 @Frequency 1e+7 Hz |
|
| 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
IEC 250 | |
| Arc Resistance | 182 sec | 182 sec | |
| Comparative Tracking Index | 200 V | 200 V | IEC 112 |