| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 | ||
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.070 % @Temperature 22.8 °C |
0.070 % @Temperature 73.0 °F |
24hr immersion; ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50%RH; ISO 62 | ||
| Viscosity Test | 110 cm³/g | 110 cm³/g | ISO 307, 1157, 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 | ||
| 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A | ||
| 93.1 MPa @Temperature 22.8 °C |
13500 psi @Temperature 73.0 °F |
ASTM D638 | |||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527-2/1A | ||
| 3.0 % @Temperature 22.8 °C |
3.0 % @Temperature 73.0 °F |
ASTM D638 | |||
| Tensile Modulus | 6.00 GPa | 870 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 | ||
| 145 MPa @Temperature 22.8 °C |
21000 psi @Temperature 73.0 °F |
ASTM D790 | |||
| Flexural Modulus | 5.60 GPa | 812 ksi | ISO 178 | ||
| 5.10 GPa @Temperature 22.8 °C |
740 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1A | ||
| 7.00 kJ/m² @Temperature 30.0 °C |
3.33 ft-lb/in² @Temperature 86.0 °F |
ISO 180/1A | |||
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.5 @Frequency 1000 Hz |
3.5 @Frequency 1000 Hz |
ASTM D150 | ||
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | short term; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ASTM D648 | ||
| 218 °C | 424 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ASTM D648 | ||
| 195 °C | 383 °F | ISO 75-1, -2 | |||
| Vicat Softening Point | 220 °C | 428 °F | B50 (50°C/h 50N); ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 0.850 mm |
HB @Thickness 0.0335 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 260 °C | 500 °F | ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Melt volume rate (MVR), cm³/10min | 17 | ||||
| MVR test load, kg | 2.16 | ||||
| MVR test temperature, °C | 250 | ||||
| Processing conditions acc. ISO | 7792-2 | ||||