| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 | ||
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.17 % | 0.17 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0070 cm/cm | 0.0010 - 0.0070 in/in | ISO 294-4 | ||
| 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 | ||
| Melt Flow | 26 g/10 min | 26 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 90 | 90 | ISO 2039-2 | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A | ||
 |
44.8 MPa @Temperature 121 °C |
6500 psi @Temperature 250 °F |
ASTM D638 | ||
| 55.2 MPa @Temperature 80.0 °C |
8000 psi @Temperature 176 °F |
ASTM D638 | |||
| 93.1 MPa @Temperature 22.8 °C |
13500 psi @Temperature 73.0 °F |
ASTM D638 | |||
| 105 MPa @Temperature 0.000 °C |
15200 psi @Temperature 32.0 °F |
ASTM D638 | |||
| 108 MPa @Temperature -40.0 °C |
15700 psi @Temperature -40.0 °F |
ASTM D638 | |||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527-2/1A | ||
| |
1.9 % @Temperature -40.0 °C |
1.9 % @Temperature -40.0 °F |
ASTM D638 | ||
| 2.0 % @Temperature 0.000 °C |
2.0 % @Temperature 32.0 °F |
ASTM D638 | |||
| 3.0 % @Temperature 22.8 °C |
3.0 % @Temperature 73.0 °F |
ASTM D638 | |||
| 6.3 % @Temperature 80.0 °C |
6.3 % @Temperature 176 °F |
ASTM D638 | |||
| 6.3 % @Temperature 121 °C |
6.3 % @Temperature 250 °F |
ASTM D638 | |||
| Tensile Modulus | 5.80 GPa | 841 ksi | 1mm/min; ISO 527-2/1A | ||
| 2.07 GPa @Temperature 121 °C |
300 ksi @Temperature 250 °F |
ASTM D638 | |||
| 2.45 GPa @Temperature 80.0 °C |
355 ksi @Temperature 176 °F |
ASTM D638 | |||
| 5.52 GPa @Temperature 22.8 °C |
800 ksi @Temperature 73.0 °F |
ASTM D638 | |||
| 6.21 GPa @Temperature 0.000 °C |
900 ksi @Temperature 32.0 °F |
ASTM D638 | |||
| 6.41 GPa @Temperature -40.0 °C |
930 ksi @Temperature -40.0 °F |
ASTM D638 | |||
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 | ||
| 145 MPa @Temperature 22.8 °C |
21000 psi @Temperature 73.0 °F |
ASTM D790 | |||
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO 178 | ||
| 4.83 GPa @Temperature 22.8 °C |
700 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eU | ||
| 2.00 J/cm² @Temperature 30.0 °C |
9.52 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA | ||
| 0.500 J/cm² @Temperature 30.0 °C |
2.38 ft-lb/in² @Temperature 86.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
ASTM D150 | ||
| 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| 4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | short term; ASTM D149 | ||
| 29.0 kV/mm | 737 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.0016 @Frequency 100 Hz |
0.0016 @Frequency 100 Hz |
IEC 60250 | ||
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
ASTM D150 | |||
| Arc Resistance | 125 sec | 125 sec | ASTM D495 | ||
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 | ||
| 350 V | 350 V | IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ASTM D648 | ||
| 215 °C | 419 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ASTM D648 | ||
| 195 °C | 383 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 215 °C | 419 °F | B50 (50°C/h 50N); ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
||||
| Oxygen Index | 20 % | 20 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 260 °C | 500 °F | ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Processing conditions acc. ISO | 7792-2 | ||||