| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Linear Mold Shrinkage | 0.0015 cm/cm @Thickness 2.00 mm |
0.0015 in/in @Thickness 0.0787 in |
sheet with film gate at rim, mold temperature 80°C |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 20.4 g/10 min @Load 2.16 kg, Temperature 250 °C |
20.4 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-1/2 |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527-1/2 |
| Tensile Modulus | 14.5 GPa | 2100 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Vicat Softening Point | 210 °C | 410 °F | Method B, 50 N; ISO 306 |
| 220 °C | 428 °F | Method A, 10 N; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695 |
|