| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 | ||
| Water Absorption at Saturation | 0.70 % | 0.70 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | Pigmentation can change mold shrinkage. | ||
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | Pigmentation can change mold shrinkage. | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 80 | 80 | ISO 868 | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527-1/2 | ||
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ISO 527-1/2 | ||
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527-1/2 | ||
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
IEC 60250 | ||
| 4.1 @Frequency 100 Hz |
4.1 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.0080 @Frequency 100 Hz |
0.0080 @Frequency 100 Hz |
IEC 60250 | ||
| 0.022 @Frequency 1e+6 Hz |
0.022 @Frequency 1e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 325 V | 325 V | Test Solution A, 100 drops; IEC 60112 | ||
| 350 V | 350 V | Test Solution A, CTI; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 30.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 131 °F |
Longitudinal; ISO 11359 | ||
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
33.3 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359 | ||
| Melting Point | 221 - 226 °C | 430 - 439 °F | DSC | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ISO 75-1/2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/2 | ||
| Vicat Softening Point | 210 °C | 410 °F | 50N; ISO 306 | ||
| 222 °C | 432 °F | 10N; ISO 306 | |||
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
|||
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||||
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
||||
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-1/0-3 | ||
| De |
|||||
| Color | Black | ||||
| Electrolytic Corrosion | A1 Step | IEC 60426 |
|||