| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ISO 1183 | ||
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | ||
| 0.0050 cm/cm | 0.0050 in/in | 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | ||
| 0.010 cm/cm | 0.010 in/in | 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4 | |||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 260 °C |
16 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133-1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 180 MPa | 26100 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1, -2; 5 mm/min | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1, -2; 5 mm/min | ||
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527-1, -2; 1 mm/min | ||
| Flexural Strength | 170 MPa @Strain 3.80 % |
24700 psi @Strain 3.80 % |
2 mm/min; ISO 178-A | ||
| Flexural Yield Strength | 165 MPa @Strain 3.50 % |
23900 psi @Strain 3.50 % |
2 mm/min; ISO 178-A | ||
| Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178-A | ||
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A | ||
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |||
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | ||
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | ||
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU | |||
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA | ||
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 | ||
| Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1, -3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 205 °C @Load 5.10 kg |
401 °F @Load 11.2 lb |
120°C/hour; ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |||
| 270 °C | 518 °F | for test specimens; ISO 294 | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| 90.0 °C | 194 °F | for test specimens; ISO 294 | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4 - 8 hour | 4 - 8 hour | |||
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test | ||
| De |
|||||
| ISO Shortname | ISO 7792-1-PBT+PET, GHMR, 09-060, GF15 | ||||