朗盛B 1701 000000 PBT_产品资讯

物性表：

Physical Properties	Metric	English	Comments

Specific Gravity	1.31 g/cc	1.31 g/cc	ISO 1183
Bulk Density	0.800 g/cc	0.0289 lb/in³	ISO 60
Moisture Absorption at Equilibrium	0.20 %	0.20 %	50% RH; ISO 62
Water Absorption at Saturation	0.50 %	0.50 %	ISO 62
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
	0.020 cm/cm	0.020 in/in	60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0020 cm/cm	0.0020 in/in	Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
	0.020 cm/cm	0.020 in/in	60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 260 °C	12 g/10 min @Load 4.76 lb, Temperature 500 °F	ISO 1133-1

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	60.0 MPa	8700 psi	ISO 527-1, -2; 50 mm/min
Elongation at Break	>= 20 %	>= 20 %	ISO 527-1, -2; 50 mm/min
Elongation at Yield	9.0 %	9.0 %	ISO 527-1, -2; 50 mm/min
Tensile Modulus	2.70 GPa	392 ksi	ISO 527-1, -2; 1 mm/min
Flexural Strength	85.0 MPa @Strain 6.00 %	12300 psi @Strain 6.00 %	2 mm/min; ISO 178-A
Flexural Yield Strength	75.0 MPa @Strain 3.50 %	10900 psi @Strain 3.50 %	2 mm/min; ISO 178-A
Flexural Modulus	2.50 GPa	363 ksi	2 mm/min; ISO 178-A
Izod Impact, Notched (ISO)	<= 10.0 kJ/m² @Temperature 23.0 °C	<= 4.76 ft-lb/in² @Temperature 73.4 °F	ISO 180-1A
	<= 10.0 kJ/m² @Temperature -30.0 °C	<= 4.76 ft-lb/in² @Temperature -22.0 °F	ISO 180-1A
Izod Impact, Unnotched (ISO)	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 180-1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 180-1U
Charpy Impact Unnotched	20.0 J/cm² @Temperature -30.0 °C	95.2 ft-lb/in² @Temperature -22.0 °F	ISO 179-1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179-1eU
Charpy Impact, Notched	<= 1.00 J/cm² @Temperature 23.0 °C	<= 4.76 ft-lb/in² @Temperature 73.4 °F	ISO 179-1eA
	<= 1.00 J/cm² @Temperature -30.0 °C	<= 4.76 ft-lb/in² @Temperature -22.0 °F	ISO 179-1eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	<= 1.00e+15 ohm	<= 1.00e+15 ohm	IEC 60093
Dielectric Constant	3.2 @Frequency 1.00e+6 Hz	3.2 @Frequency 1.00e+6 Hz	IEC 60250
	3.4 @Frequency 100 Hz	3.4 @Frequency 100 Hz	IEC 60250
Dielectric Strength	30.0 kV/mm @Thickness 1.00 mm	762 kV/in @Thickness 0.0394 in	IEC 60243-1
Dissipation Factor	0.0015 @Frequency 100 Hz	0.0015 @Frequency 100 Hz	IEC 60250
	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	d.a.m.; Solution A; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	120 µm/m-°C @Temperature 23.0 - 55.0 °C	66.7 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1, -2
CTE, linear, Transverse to Flow	120 µm/m-°C @Temperature 23.0 - 55.0 °C	66.7 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1, -2
Melting Point	225 °C	437 °F	10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi)	140 °C	284 °F	ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F	ISO 75-1, -2
Vicat Softening Point	180 °C @Load 5.10 kg	356 °F @Load 11.2 lb	120°C/hour; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in

Processing Properties	Metric	English	Comments
Melt Temperature	260 °C	500 °F	for test specimens; ISO 294
Mold Temperature	80.0 °C	176 °F	for test specimens; ISO 294
Drying Temperature	120 °C	248 °F
Dry Time	4 - 8 hour	4 - 8 hour
Moisture Content	0.00 - 0.020 %	0.00 - 0.020 %	residual; Karl Fischer Test

Descriptive Properties
ISO Shortname	ISO 7792-1-PBT, GM, 13-030

图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！

我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！

欢迎新老客户来电或QQ咨询：

联系人：李先生

联系电话；13636696005

联系QQ；1020580970

联系邮箱；1020580970@qq.com