朗盛/T 7331 pos151 700226/30%玻纤

朗盛Pocan®T 7331 pos151 700226 PBT +PET,30%玻璃纤维 类别:聚合物;热塑性;聚酯,TP;聚对苯二甲酸丁二醇酯(PBT);PBT、PET共混,填充玻璃;聚对苯二甲酸乙二醇酯(PET) 材料说明:PBT +宠物,30%的玻璃纤维,注射成型,提高表面光洁度,增加温度峰值负载,紫外线稳定
 物性表:

 
Physical Properties Metric English Comments
Specific Gravity  1.55 g/cc 1.55 g/cc ISO 1183
Bulk Density  0.800 g/cc 0.0289 lb/in³ ISO 60
Moisture Absorption at Equilibrium  0.10 % 0.10 % 50% RH; ISO 62
Water Absorption at Saturation  0.30 % 0.30 % ISO 62
Viscosity Test  91 cm³/g 91 cm³/g Viscosity number; ISO 1628-5
Linear Mold Shrinkage, Flow  0.0010 cm/cm 0.0010 in/in Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
  0.0030 cm/cm 0.0030 in/in 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse  0.0020 cm/cm 0.0020 in/in Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
  0.0090 cm/cm 0.0090 in/in 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4
Melt Flow  30 g/10 min
@Load 5.00 kg,
Temperature 260 °C
30 g/10 min
@Load 11.0 lb,
Temperature 500 °F
ISO 1133-1
 
Mechanical Properties Metric English Comments
Ball Indentation Hardness  200 MPa 29000 psi ISO 2039-1
Tensile Strength at Break  145 MPa 21000 psi ISO 527-1, -2; 5 mm/min
Elongation at Break  2.8 % 2.8 % ISO 527-1, -2; 5 mm/min
Tensile Modulus  10.4 GPa 1510 ksi ISO 527-1, -2; 1 mm/min
Flexural Strength  230 MPa
@Strain 3.00 %
33400 psi
@Strain 3.00 %
2 mm/min; ISO 178-A
Flexural Modulus  10.3 GPa 1490 ksi 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO)   <= 10.0 kJ/m²
@Temperature 23.0 °C
<= 4.76 ft-lb/in²
@Temperature 73.4 °F
ISO 180-1A
  <= 10.0 kJ/m²
@Temperature -30.0 °C
<= 4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 180-1A
  <= 10.0 kJ/m²
@Temperature -40.0 °C
<= 4.76 ft-lb/in²
@Temperature -40.0 °F
ISO 180-1A
Izod Impact, Unnotched (ISO)   55.0 kJ/m²
@Temperature 23.0 °C
26.2 ft-lb/in²
@Temperature 73.4 °F
ISO 180-1U
  55.0 kJ/m²
@Temperature -30.0 °C
26.2 ft-lb/in²
@Temperature -22.0 °F
ISO 180-1U
Charpy Impact Unnotched   5.50 J/cm²
@Temperature -30.0 °C
26.2 ft-lb/in²
@Temperature -22.0 °F
ISO 179-1eU
  6.50 J/cm²
@Temperature 23.0 °C
30.9 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1eU
Charpy Impact, Notched   <= 1.00 J/cm²
@Temperature 23.0 °C
<= 4.76 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1eA
  <= 1.00 J/cm²
@Temperature -30.0 °C
<= 4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 179-1eA
Puncture Energy  2.10 J
@Load <=66.3 kg,
Temperature 23.0 °C
1.55 ft-lb
@Load <=146 lb,
Temperature 73.4 °F
ISO 6603-2
Tensile Creep Modulus, 1 hour  10000 MPa 1.45e+6 psi ISO 899-1
Tensile Creep Modulus, 1000 hours  8500 MPa 1.23e+6 psi ISO 899-1
 
Electrical Properties Metric English Comments
Dielectric Constant   3.8
@Frequency 1.00e+6 Hz
3.8
@Frequency 1.00e+6 Hz
IEC 60250
  4.0
@Frequency 100 Hz
4.0
@Frequency 100 Hz
IEC 60250
Dielectric Strength  27.0 kV/mm
@Thickness 1.00 mm
686 kV/in
@Thickness 0.0394 in
IEC 60243-1
Comparative Tracking Index  250 V 250 V d.a.m.; Solution A; IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  30.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
16.7 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1, -2
CTE, linear, Transverse to Flow  60.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
33.3 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1, -2
Thermal Conductivity  0.270 W/m-K 1.87 BTU-in/hr-ft²-°F ISO 8302
Melting Point  225 - 250 °C 437 - 482 °F 10°C/min; ISO 11357-1, -3
Maximum Service Temperature, Air  140 °C 284 °F IEC 60216-1, Tensile impact strength, 20000 h
  155 °C 311 °F IEC 60216-1, Tensile strength, 20000 h
  155 °C 311 °F IEC 60216-1, Electric strength, 20000 h
  220 °C 428 °F Resistance to heat - ball pressure test; IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi)  220 °C 428 °F ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi)  200 °C 392 °F ISO 75-1, -2
Vicat Softening Point  205 °C
@Load 5.10 kg
401 °F
@Load 11.2 lb
120°C/hour; ISO 306
UL RTI, Electrical  140 °C 284 °F UL 746B
UL RTI, Mechanical with Impact  125 °C 257 °F UL 746B
UL RTI, Mechanical without Impact  140 °C 284 °F UL 746B
Flammability, UL94   HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
 
  HB
@Thickness 0.800 mm
HB
@Thickness 0.0315 in
 
Oxygen Index  21 % 21 % Method A; ISO 4589-2
Glow Wire Test  750 °C
@Diameter 2.00 mm
1380 °F
@Diameter 0.0787 in
GWFI; IEC 60695-2-12
 
Processing Properties Metric English Comments
Melt Temperature  260 - 280 °C 500 - 536 °F  
  270 °C 518 °F for test specimens; ISO 294
Mold Temperature  80.0 - 100 °C 176 - 212 °F  
  90.0 °C 194 °F for test specimens; ISO 294
Drying Temperature  120 °C 248 °F  
Dry Time  4 - 8 hour 4 - 8 hour  
Moisture Content  0.00 - 0.020 % 0.00 - 0.020 % residual; Karl Fischer Test
 
Descriptive Properties
Electrolytic Corrosion IEC 60426 A 1
Halving Interval (°C) 10.2 IEC 60216-1, Tensile strength
  10.2 IEC 60216-1, Electric strength
  13.5 IEC 60216-1, Tensile impact strength
ISO Shortname ISO 7792-1-PBT+PET, GHlMR, 09-100, GF30
图:

上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李先生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41262.html

免责声明: 本文 朗盛/T 7331 pos151 700226/30%玻纤 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4