朗盛Pocan®B 1100 000000 PBT

朗盛Pocan®B 1100 000000 PBT 类别:聚合物;热塑性;聚酯,TP;聚对苯二甲酸丁二醇酯(PBT);聚对苯二甲酸丁二醇酯(PBT),无筋,成型 材料说明:PBT,无筋,挤出,注射成型,提高流动性
 物性表

 
Physical Properties Metric English Comments
Density  1.30 g/cc 0.0470 lb/in³ ISO 1183
Water Absorption  0.50 % 0.50 % Test Sim. to ISO 62
Moisture Absorption at Equilibrium  0.20 % 0.20 % 23°C/50% R.H.; Test Sim. to ISO 62
Melt Flow  104 g/10 min
@Load 2.16 kg,
Temperature 250 °C
104 g/10 min
@Load 4.76 lb,
Temperature 482 °F
Estimated using room temperature density; ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Modulus  2.70 GPa 392 ksi ISO 527-1/-2
Charpy Impact Unnotched   9.00 J/cm²
@Temperature -30.0 °C
42.8 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eU
  13.0 J/cm²
@Temperature 23.0 °C
61.9 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched   <= 1.00 J/cm²
@Temperature -30.0 °C
<= 4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eA
  <= 1.00 J/cm²
@Temperature 23.0 °C
<= 4.76 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  >= 1.00e+15 ohm >= 1.00e+15 ohm IEC 60093
Dielectric Constant   3.2
@Frequency 1.00e+6 Hz
3.2
@Frequency 1.00e+6 Hz
IEC 60250
  3.4
@Frequency 100 Hz
3.4
@Frequency 100 Hz
IEC 60250
Dissipation Factor   0.0020
@Frequency 100 Hz
0.0020
@Frequency 100 Hz
IEC 60250
  0.019
@Frequency 1.00e+6 Hz
0.019
@Frequency 1.00e+6 Hz
IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  130 µm/m-°C 72.2 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  130 µm/m-°C 72.2 µin/in-°F ISO 11359-1/-2
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  160 °C 320 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  60.0 °C 140 °F ISO 75-1/-2
Vicat Softening Point  170 °C 338 °F 50°C/h 50N; ISO 306
Flammability, UL94  HB HB IEC 60695-11-10
  HB
@Thickness 0.800 mm
HB
@Thickness 0.0315 in
IEC 60695-11-10
Oxygen Index  24 % 24 % ISO 4589-1/-2
 
Processing Properties Metric English Comments
Melt Temperature  260 °C 500 °F Injection Molding; ISO 294
Mold Temperature  80.0 °C 176 °F Injection Molding; ISO 10724
 
Descriptive Properties
Additives Release agent  
Form Pellets  
ISO Shortname ISO 7792-1-PBT,G,07-030  
Processing Coating  
  Film extrusion  
  Injection molding  
Region Asia Pacific  
  Europe  
  Near East/Africa  
  North America  
  South and Central America
图:

上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李先生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41267.html

免责声明: 本文 朗盛Pocan®B 1100 000000 PBT 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4