| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| 1.19 g/cc @Temperature 200 °C |
0.0430 lb/in³ @Temperature 392 °F |
Melt | |
| Linear Mold Shrinkage, Flow | 0.0220 cm/cm | 0.0220 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0180 cm/cm | 0.0180 in/in | ISO 294-4, 2577 |
| Melt Flow | 2.20 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 91.0 | 91.0 | ISO 2039-2 |
| Hardness, Rockwell R | 121 | 121 | ISO 2039-2 |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50.0 % | >= 50.0 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 23.0 % | 23.0 % | ISO 527-1/-2 |
| Tensile Modulus | 3.15 GPa | 457 ksi | ISO 527-1/-2 |
| 0.728 GPa @Temperature 120 °C |
106 ksi @Temperature 248 °F |
ISO 11403-1,-2 | |
| 3.088 GPa @Temperature 23.0 °C |
447.9 ksi @Temperature 73.4 °F |
ISO 11403-1,-2 | |
| 3.151 GPa @Temperature 0.000 °C |
457.0 ksi @Temperature 32.0 °F |
ISO 11403-1,-2 | |
| 3.866 GPa @Temperature -40.0 °C |
560.7 ksi @Temperature -40.0 °F |
ISO 11403-1,-2 | |
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 180/1A |
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact, Notched | 1.05 J/cm² @Temperature -30.0 °C |
5.00 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.90 @Frequency 1.00e+6 Hz |
3.90 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.00 @Frequency 100 Hz |
4.00 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 45.0 kV/mm | 1140 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.000500 @Frequency 100 Hz |
0.000500 @Frequency 100 Hz |
IEC 60250 |
| 0.00600 @Frequency 1.00e+6 Hz |
0.00600 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| 100 µm/m-°C @Temperature -40.0 - 23.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| 100 µm/m-°C @Temperature -40.0 - 23.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75-1/-2 |
| Annealing Point | 160 °C | 320 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 | |
| Flame Spread | 37.0 mm/min @Thickness 1.00 mm |
1.46 in/min @Thickness 0.0394 in |
Burning rate; ISO 3795 (FMVSS 302) |