| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0210 cm/cm | 0.0210 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0150 cm/cm | 0.0150 in/in | ISO 294-4, 2577 |
| Melt Flow | 1.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527-1/-2 |
| Elongation at Break | 15.0 % | 15.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ISO 75-1/-2 |
| Annealing Point | 160 °C | 320 °F | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 200 °C | 392 °F | Optimum |
| >= 210 °C | >= 410 °F | ||
| 215 °C | 419 °F | Optimum | |
| <= 220 °C | <= 428 °F | ||
| Mold Temperature | >= 80.0 °C | >= 176 °F | |
| 90.0 °C | 194 °F | Optimum | |
| <= 100 °C | <= 212 °F | ||
| Drying Temperature | 75.0 °C @Time 7200 - 14400 sec |
167 °F @Time 2.00 - 4.00 hour |
|
| 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
||
| 85.0 °C @Time 7200 - 14400 sec |
185 °F @Time 2.00 - 4.00 hour |
||
| Moisture Content | 0.200 % | 0.200 % | |
| Hold Pressure | 90.0 - 110 MPa | 13100 - 16000 psi | |