巴斯夫/ N 2200 G53 UNC q600 25%玻璃填充POM_产品资讯

物性表：

Physical Properties	Metric	English	Comments

Density	1.58 g/cc	0.0571 lb/in³	ISO 1183
Water Absorption	0.90 %	0.90 %	ISO 62
Moisture Absorption at Equilibrium	0.15 %	0.15 %	23°C/50% R.H.; ISO 62
Melt Flow	5.5 g/10 min @Load 2.16 kg, Temperature 190 °C	5.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	190 MPa	27600 psi	ISO2039
Tensile Strength at Break	130 MPa	18900 psi	5mm/min; ISO 527
Tensile Stress	10.0 MPa @Strain 0.200 %, Time 3.60e+7 sec	1450 psi @Strain 0.200 %, Time 10000 hour	ISO 899-1
	12.0 MPa @Strain 0.200 %, Time 3.60e+6 sec	1740 psi @Strain 0.200 %, Time 1000 hour	ISO 899-1
	15.0 MPa @Strain 0.200 %, Time 3600 sec	2180 psi @Strain 0.200 %, Time 1.00 hour	ISO 899-1
	31.0 MPa @Strain 0.600 %, Time 3.60e+6 sec	4500 psi @Strain 0.600 %, Time 1000 hour	ISO 899-1
	32.0 MPa @Strain 0.600 %, Time 3.60e+7 sec	4640 psi @Strain 0.600 %, Time 10000 hour	ISO 899-1
	35.0 MPa @Strain 0.500 %, Time 3600 sec	5080 psi @Strain 0.500 %, Time 1.00 hour	ISO 899-1
	55.0 MPa @Strain 1.40 %, Time 3.60e+6 sec	7980 psi @Strain 1.40 %, Time 1000 hour	ISO 899-1
	55.0 MPa @Strain 1.80 %, Time 3.60e+7 sec	7980 psi @Strain 1.80 %, Time 10000 hour	ISO 899-1
	58.0 MPa @Strain 0.800 %, Time 3600 sec	8410 psi @Strain 0.800 %, Time 1.00 hour	ISO 899-1
Tensile Strength, Yield	60.0 MPa @Temperature 120 °C	8700 psi @Temperature 248 °F	ISO 527
	90.0 MPa @Temperature 80.0 °C	13100 psi @Temperature 176 °F	ISO 527
	125 MPa @Temperature 40.0 °C	18100 psi @Temperature 104 °F	ISO 527
Elongation at Break	3.0 %	3.0 %	5mm/min; ISO 527
Modulus of Elasticity	8.80 GPa	1280 ksi	ISO 527
	2.50 GPa @Temperature 140 °C	363 ksi @Temperature 284 °F	SIO 527
	5.00 GPa @Temperature 100 °C	725 ksi @Temperature 212 °F	SIO 527
	8.10 GPa @Temperature 40.0 °C	1170 ksi @Temperature 104 °F	SIO 527
Izod Impact, Notched (ISO)	9.00 kJ/m²	4.28 ft-lb/in²	ISO 180
	9.00 kJ/m² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	ISO 180
Charpy Impact Unnotched	5.50 J/cm²	26.2 ft-lb/in²	ISO 179
	6.00 J/cm² @Temperature -30.0 °C	28.6 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.900 J/cm²	4.28 ft-lb/in²	ISO 179
	0.880 J/cm² @Temperature -30.0 °C	4.19 ft-lb/in² @Temperature -22.0 °F	ISO 179
Tensile Creep Modulus, 1000 hours	5800 MPa	841000 psi	ISO 899

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	IEC 60093
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm	IEC 60093
Dielectric Constant	4.0 @Frequency 100 Hz	4.0 @Frequency 100 Hz	IEC 60250
	4.0 @Frequency 1.00e+6 Hz	4.0 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	43.0 kV/mm	1090 kV/in	IEC 60243-1
Dissipation Factor	0.0040 @Frequency 100 Hz	0.0040 @Frequency 100 Hz	IEC 60250
	0.0070 @Frequency 1.00e+6 Hz	0.0070 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test Solution A; IEC 60112
	600 V	600 V	Test Solution B; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	4.00 µm/m-°C @Temperature 23.0 - 55.0 °C	2.22 µin/in-°F @Temperature 73.4 - 131 °F	DIN 53752
Melting Point	168 °C	334 °F	DIN 53765
Maximum Service Temperature, Air	110 °C	230 °F
Deflection Temperature at 1.8 MPa (264 psi)	163 °C	325 °F	ISO 75
Vicat Softening Point	160 °C	320 °F	(50 °C/h / 50N) - B/50; ISO 306

Processing Properties	Metric	English	Comments
Melt Temperature	190 - 230 °C	374 - 446 °F
Mold Temperature	60.0 - 120 °C	140 - 248 °F

Descriptive Properties
Color	Natural
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding

图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！

我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！

欢迎新老客户来电或QQ咨询：

联系人：李先生

联系电话；13636696005

联系QQ；1020580970

联系邮箱；1020580970@qq.com