| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.900 g/cc | 0.0217 - 0.0325 lb/in³ | |||
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62 | ||
| Viscosity Measurement | 107 | 107 | [cm3/g]; ISO 307 | ||
| Linear Mold Shrinkage, Flow | 0.0039 cm/cm | 0.0039 in/in | plate with film gate 150x150x3mm3 | ||
| 0.0043 cm/cm | 0.0043 in/in | ISO 2577 | |||
| Linear Mold Shrinkage, Transverse | 0.0116 cm/cm | 0.0116 in/in | ISO 2577 | ||
| 0.0128 cm/cm | 0.0128 in/in | plate with film gate 150x150x3mm3 | |||
| Melt Flow | 20.3 g/10 min @Load 2.16 kg, Temperature 250 °C |
20.3 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 180 MPa @Load 98.0 kg, Time 30.0 sec |
26100 psi @Load 216 lb, Time 0.00833 hour |
ISO 2039-1 | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.5 % | 3.5 % | ISO 524-1/-2 | ||
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527-1-2 | ||
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 | ||
| Charpy Impact Unnotched | 5.40 J/cm² @Temperature -30.0 °C |
25.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 5.80 J/cm² @Temperature 23.0 °C |
27.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |||
| Dissipation Factor | 0.0012 @Frequency 100 Hz |
0.0012 @Frequency 100 Hz |
IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 150 V | 150 V | Test Solution B; IEC 60112 | ||
| 300 V | 300 V | Test Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 - 40.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
16.7 - 22.2 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 | ||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612-1 | ||
| Melting Point | 223 °C | 433 °F | ISO 11357-1/-2 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | at 50% loss of tensile strength after 20,000hr | ||
| 150 °C | 302 °F | at 50% loss of tensile strength after 5,000hr | |||
| 210 °C | 410 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness >=0.400 mm |
HB @Thickness >=0.0157 in |
IEC 60695-11-10 | ||
| HB @Thickness >=4.00 mm |
HB @Thickness >=0.157 in |
by electrical sources of ignition, Method BH; IEC 60707 | |||
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding/Extrusion | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection molding | ||
| De |
|||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350°C | ASTM D1929 |
|||