Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 | ||
Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | ||
Filler Content | 30 % | 30 % | |||
Water Absorption | 0.060 % @Temperature 23.0 °C |
0.060 % @Temperature 73.4 °F |
50%RH,23°C,24h; ASTM D570 | ||
Viscosity | 110000 cP @Shear Rate 3090 1/s, Temperature 305 °C |
110000 cP @Shear Rate 3090 1/s, Temperature 581 °F |
ISO 11443 | ||
138000 cP @Shear Rate 3090 1/s, Temperature 290 °C |
138000 cP @Shear Rate 3090 1/s, Temperature 554 °F |
ISO 11443 | |||
157000 cP @Shear Rate 1450 1/s, Temperature 305 °C |
157000 cP @Shear Rate 1450 1/s, Temperature 581 °F |
ISO 11443 | |||
172000 cP @Shear Rate 3090 1/s, Temperature 275 °C |
172000 cP @Shear Rate 3090 1/s, Temperature 527 °F |
ISO 11443 | |||
215000 cP @Shear Rate 1450 1/s, Temperature 290 °C |
215000 cP @Shear Rate 1450 1/s, Temperature 554 °F |
ISO 11443 | |||
218000 cP @Shear Rate 681 1/s, Temperature 305 °C |
218000 cP @Shear Rate 681 1/s, Temperature 581 °F |
ISO 11443 | |||
260000 cP @Shear Rate 1450 1/s, Temperature 275 °C |
260000 cP @Shear Rate 1450 1/s, Temperature 527 °F |
ISO 11443 | |||
318000 cP @Shear Rate 681 1/s, Temperature 290 °C |
318000 cP @Shear Rate 681 1/s, Temperature 554 °F |
ISO 11443 | |||
322000 cP @Shear Rate 316 1/s, Temperature 305 °C |
322000 cP @Shear Rate 316 1/s, Temperature 581 °F |
ISO 11443 | |||
386000 cP @Shear Rate 681 1/s, Temperature 275 °C |
386000 cP @Shear Rate 681 1/s, Temperature 527 °F |
ISO 11443 | |||
454000 cP @Shear Rate 316 1/s, Temperature 290 °C |
454000 cP @Shear Rate 316 1/s, Temperature 554 °F |
ISO 11443 | |||
463000 cP @Shear Rate 146 1/s, Temperature 305 °C |
463000 cP @Shear Rate 146 1/s, Temperature 581 °F |
ISO 11443 | |||
560000 cP @Shear Rate 316 1/s, Temperature 275 °C |
560000 cP @Shear Rate 316 1/s, Temperature 527 °F |
ISO 11443 | |||
655000 cP @Shear Rate 146 1/s, Temperature 290 °C |
655000 cP @Shear Rate 146 1/s, Temperature 554 °F |
ISO 11443 | |||
663000 cP @Shear Rate 73.0 1/s, Temperature 305 °C |
663000 cP @Shear Rate 73.0 1/s, Temperature 581 °F |
ISO 11443 | |||
810000 cP @Shear Rate 146 1/s, Temperature 275 °C |
810000 cP @Shear Rate 146 1/s, Temperature 527 °F |
ISO 11443 | |||
935000 cP @Shear Rate 73.0 1/s, Temperature 290 °C |
935000 cP @Shear Rate 73.0 1/s, Temperature 554 °F |
ISO 11443 | |||
1.00e+6 cP @Shear Rate 36.0 1/s, Temperature 305 °C |
1.00e+6 cP @Shear Rate 36.0 1/s, Temperature 581 °F |
ISO 11443 | |||
1.17e+6 cP @Shear Rate 73.0 1/s, Temperature 275 °C |
1.17e+6 cP @Shear Rate 73.0 1/s, Temperature 527 °F |
ISO 11443 | |||
1.29e+6 cP @Shear Rate 36.0 1/s, Temperature 290 °C |
1.29e+6 cP @Shear Rate 36.0 1/s, Temperature 554 °F |
ISO 11443 | |||
1.62e+6 cP @Shear Rate 36.0 1/s, Temperature 275 °C |
1.62e+6 cP @Shear Rate 36.0 1/s, Temperature 527 °F |
ISO 11443 | |||
1.73e+6 cP @Shear Rate 12.0 1/s, Temperature 305 °C |
1.73e+6 cP @Shear Rate 12.0 1/s, Temperature 581 °F |
ISO 11443 | |||
1.97e+6 cP @Shear Rate 7.30 1/s, Temperature 305 °C |
1.97e+6 cP @Shear Rate 7.30 1/s, Temperature 581 °F |
ISO 11443 | |||
2.55e+6 cP @Shear Rate 12.0 1/s, Temperature 290 °C |
2.55e+6 cP @Shear Rate 12.0 1/s, Temperature 554 °F |
ISO 11443 | |||
2.96e+6 cP @Shear Rate 12.0 1/s, Temperature 275 °C |
2.96e+6 cP @Shear Rate 12.0 1/s, Temperature 527 °F |
ISO 11443 | |||
3.33e+6 cP @Shear Rate 7.30 1/s, Temperature 290 °C |
3.33e+6 cP @Shear Rate 7.30 1/s, Temperature 554 °F |
ISO 11443 | |||
4.11e+6 cP @Shear Rate 7.30 1/s, Temperature 275 °C |
4.11e+6 cP @Shear Rate 7.30 1/s, Temperature 527 °F |
ISO 11443 | |||
Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
Flow | ||
0.0021 cm/cm @Thickness 1.60 mm |
0.0021 in/in @Thickness 0.0630 in |
Flow | |||
0.0063 cm/cm @Thickness 1.60 mm |
0.0063 in/in @Thickness 0.0630 in |
Transverse | |||
0.0075 cm/cm @Thickness 3.20 mm |
0.0075 in/in @Thickness 0.126 in |
Transverse | |||
Linear Mold Shrinkage, Flow | 0.0035 cm/cm | 0.0035 in/in | Annealed; ISO 294-4 | ||
0.0025 cm/cm @Thickness 2.00 mm |
0.0025 in/in @Thickness 0.0787 in |
ISO 294-4 | |||
Linear Mold Shrinkage, Transverse | 0.0105 cm/cm | 0.0105 in/in | Annealed; ISO 294-4 | ||
0.0085 cm/cm @Thickness 2.00 mm |
0.0085 in/in @Thickness 0.0787 in |
ISO 294-4 | |||
Melt Index of Compound | 5.5 g/10 min @Load 5.00 kg, Temperature 280 °C |
5.5 g/10 min @Load 11.0 lb, Temperature 536 °F |
cm3/10 min; ISO 1133 | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Rockwell M | 70 | 70 | ASTM D785 | ||
70 | 70 | ISO 2039/2 | |||
Hardness, Rockwell R | 115 | 115 | ASTM D785 | ||
115 | 115 | ISO 2039/2 | |||
Tensile Strength at Break | 125 MPa @Temperature 23.0 °C |
18100 psi @Temperature 73.4 °F |
ISO 527 | ||
Tensile Strength | 55.2 MPa @Temperature 150 °C |
8010 psi @Temperature 302 °F |
ASTM D638 | ||
70.3 MPa @Temperature 90.0 °C |
10200 psi @Temperature 194 °F |
ASTM D638 | |||
126 MPa @Temperature 23.0 °C |
18300 psi @Temperature 73.4 °F |
ASTM D638 | |||
206 MPa @Temperature -40.0 °C |
29900 psi @Temperature -40.0 °F |
ASTM D638 | |||
Tensile Stress | 20.5 MPa @Strain 1.05 %, Temperature 150 °C |
2970 psi @Strain 1.05 %, Temperature 302 °F |
ISO 527 | ||
23.5 MPa @Strain 0.230 %, Temperature 0.000 °C |
3410 psi @Strain 0.230 %, Temperature 32.0 °F |
ISO 527 | |||
23.5 MPa @Strain 0.960 %, Temperature 120 °C |
3410 psi @Strain 0.960 %, Temperature 248 °F |
ISO 527 | |||
24.5 MPa @Strain 0.260 %, Temperature 40.0 °C |
3550 psi @Strain 0.260 %, Temperature 104 °F |
ISO 527 | |||
25.6 MPa @Strain 0.240 %, Temperature -40.0 °C |
3710 psi @Strain 0.240 %, Temperature -40.0 °F |
ISO 527 | |||
28.8 MPa @Strain 0.960 %, Temperature 90.0 °C |
4180 psi @Strain 0.960 %, Temperature 194 °F |
ISO 527 | |||
30.4 MPa @Strain 2.10 %, Temperature 150 °C |
4410 psi @Strain 2.10 %, Temperature 302 °F |
ISO 527 | |||
35.2 MPa @Strain 0.600 %, Temperature 60.0 °C |
5110 psi @Strain 0.600 %, Temperature 140 °F |
ISO 527 | |||
35.9 MPa @Strain 1.92 %, Temperature 120 °C |
5210 psi @Strain 1.92 %, Temperature 248 °F |
ISO 527 | |||
36.1 MPa @Strain 3.16 %, Temperature 150 °C |
5240 psi @Strain 3.16 %, Temperature 302 °F |
ISO 527 | |||
40.4 MPa @Strain 4.21 %, Temperature 150 °C |
5860 psi @Strain 4.21 %, Temperature 302 °F |
ISO 527 | |||
42.7 MPa @Strain 2.88 %, Temperature 120 °C |
6190 psi @Strain 2.88 %, Temperature 248 °F |
ISO 527 | |||
44.0 MPa @Strain 5.27 %, Temperature 150 °C |
6380 psi @Strain 5.27 %, Temperature 302 °F |
ISO 527 | |||
44.9 MPa @Strain 0.460 %, Temperature 0.000 °C |
6510 psi @Strain 0.460 %, Temperature 32.0 °F |
ISO 527 | |||
45.0 MPa @Strain 1.92 %, Temperature 90.0 °C |
6530 psi @Strain 1.92 %, Temperature 194 °F |
ISO 527 | |||
45.2 MPa @Strain 0.530 %, Temperature 40.0 °C |
6560 psi @Strain 0.530 %, Temperature 104 °F |
ISO 527 | |||
46.8 MPa @Strain 6.32 %, Temperature 150 °C |
6790 psi @Strain 6.32 %, Temperature 302 °F |
ISO 527 | |||
47.5 MPa @Strain 3.84 %, Temperature 120 °C |
6890 psi @Strain 3.84 %, Temperature 248 °F |
ISO 527 | |||
49.4 MPa @Strain 7.37 %, Temperature 150 °C |
7160 psi @Strain 7.37 %, Temperature 302 °F |
ISO 527 | |||
49.5 MPa @Strain 0.480 %, Temperature -40.0 °C |
7180 psi @Strain 0.480 %, Temperature -40.0 °F |
ISO 527 | |||
51.3 MPa @Strain 4.81 %, Temperature 120 °C |
7440 psi @Strain 4.81 %, Temperature 248 °F |
ISO 527 | |||
51.4 MPa @Strain 8.43 %, Temperature 150 °C |
7450 psi @Strain 8.43 %, Temperature 302 °F |
ISO 527 | |||
53.0 MPa @Strain 9.49 %, Temperature 150 °C |
7690 psi @Strain 9.49 %, Temperature 302 °F |
ISO 527 | |||
53.6 MPa @Strain 2.88 %, Temperature 90.0 °C |
7770 psi @Strain 2.88 %, Temperature 194 °F |
ISO 527 | |||
54.2 MPa @Strain 5.77 %, Temperature 120 °C |
7860 psi @Strain 5.77 %, Temperature 248 °F |
ISO 527 | |||
54.5 MPa @Strain 10.5 %, Temperature 150 °C |
7900 psi @Strain 10.5 %, Temperature 302 °F |
ISO 527 | |||
56.5 MPa @Strain 6.73 %, Temperature 120 °C |
8190 psi @Strain 6.73 %, Temperature 248 °F |
ISO 527 | |||
58.3 MPa @Strain 7.69 %, Temperature 120 °C |
8460 psi @Strain 7.69 %, Temperature 248 °F |
ISO 527 | |||
58.4 MPa @Strain 1.20 %, Temperature 60.0 °C |
8470 psi @Strain 1.20 %, Temperature 140 °F |
ISO 527 | |||
59.5 MPa @Strain 3.84 %, Temperature 90.0 °C |
8630 psi @Strain 3.84 %, Temperature 194 °F |
ISO 527 | |||
59.6 MPa @Strain 8.65 %, Temperature 120 °C |
8640 psi @Strain 8.65 %, Temperature 248 °F |
ISO 527 | |||
60.7 MPa @Strain 9.61 %, Temperature 120 °C |
8800 psi @Strain 9.61 %, Temperature 248 °F |
ISO 527 | |||
63.2 MPa @Strain 0.790 %, Temperature 40.0 °C |
9170 psi @Strain 0.790 %, Temperature 104 °F |
ISO 527 | |||
63.3 MPa @Strain 4.81 %, Temperature 90.0 °C |
9180 psi @Strain 4.81 %, Temperature 194 °F |
ISO 527 | |||
63.9 MPa @Strain 0.680 %, Temperature 0.000 °C |
9270 psi @Strain 0.680 %, Temperature 32.0 °F |
ISO 527 | |||
66.1 MPa @Strain 5.77 %, Temperature 90.0 °C |
9590 psi @Strain 5.77 %, Temperature 194 °F |
ISO 527 | |||
68.1 MPa @Strain 6.73 %, Temperature 90.0 °C |
9880 psi @Strain 6.73 %, Temperature 194 °F |
ISO 527 | |||
69.6 MPa @Strain 7.69 %, Temperature 90.0 °C |
10100 psi @Strain 7.69 %, Temperature 194 °F |
ISO 527 | |||
70.6 MPa @Strain 8.65 %, Temperature 90.0 °C |
10200 psi @Strain 8.65 %, Temperature 194 °F |
ISO 527 | |||
71.3 MPa @Strain 9.61 %, Temperature 90.0 °C |
10300 psi @Strain 9.61 %, Temperature 194 °F |
ISO 527 | |||
72.1 MPa @Strain 1.81 %, Temperature 60.0 °C |
10500 psi @Strain 1.81 %, Temperature 140 °F |
ISO 527 | |||
72.4 MPa @Strain 0.720 %, Temperature -40.0 °C |
10500 psi @Strain 0.720 %, Temperature -40.0 °F |
ISO 527 | |||
77.2 MPa @Strain 1.05 %, Temperature 40.0 °C |
11200 psi @Strain 1.05 %, Temperature 104 °F |
ISO 527 | |||
79.2 MPa @Strain 2.41 %, Temperature 60.0 °C |
11500 psi @Strain 2.41 %, Temperature 140 °F |
ISO 527 | |||
81.3 MPa @Strain 0.910 %, Temperature 0.000 °C |
11800 psi @Strain 0.910 %, Temperature 32.0 °F |
ISO 527 | |||
83.0 MPa @Strain 3.01 %, Temperature 60.0 °C |
12000 psi @Strain 3.01 %, Temperature 140 °F |
ISO 527 | |||
84.6 MPa @Strain 3.61 %, Temperature 60.0 °C |
12300 psi @Strain 3.61 %, Temperature 140 °F |
ISO 527 | |||
85.8 MPa @Strain 4.21 %, Temperature 60.0 °C |
12400 psi @Strain 4.21 %, Temperature 140 °F |
ISO 527 | |||
86.5 MPa @Strain 4.81 %, Temperature 60.0 °C |
12500 psi @Strain 4.81 %, Temperature 140 °F |
ISO 527 | |||
86.8 MPa @Strain 5.41 %, Temperature 60.0 °C |
12600 psi @Strain 5.41 %, Temperature 140 °F |
ISO 527 | |||
87.2 MPa @Strain 6.02 %, Temperature 60.0 °C |
12600 psi @Strain 6.02 %, Temperature 140 °F |
ISO 527 | |||
87.8 MPa @Strain 1.32 %, Temperature 40.0 °C |
12700 psi @Strain 1.32 %, Temperature 104 °F |
ISO 527 | |||
93.0 MPa @Strain 0.960 %, Temperature -40.0 °C |
13500 psi @Strain 0.960 %, Temperature -40.0 °F |
ISO 527 | |||
95.5 MPa @Strain 1.58 %, Temperature 40.0 °C |
13900 psi @Strain 1.58 %, Temperature 104 °F |
ISO 527 | |||
96.6 MPa @Strain 1.14 %, Temperature 0.000 °C |
14000 psi @Strain 1.14 %, Temperature 32.0 °F |
ISO 527 | |||
101 MPa @Strain 1.84 %, Temperature 40.0 °C |
14600 psi @Strain 1.84 %, Temperature 104 °F |
ISO 527 | |||
104 MPa @Strain 2.11 %, Temperature 40.0 °C |
15100 psi @Strain 2.11 %, Temperature 104 °F |
ISO 527 | |||
106 MPa @Strain 2.37 %, Temperature 40.0 °C |
15400 psi @Strain 2.37 %, Temperature 104 °F |
ISO 527 | |||
107 MPa @Strain 2.63 %, Temperature 40.0 °C |
15500 psi @Strain 2.63 %, Temperature 104 °F |
ISO 527 | |||
109 MPa @Strain 1.37 %, Temperature 0.000 °C |
15800 psi @Strain 1.37 %, Temperature 32.0 °F |
ISO 527 | |||
112 MPa @Strain 1.20 %, Temperature -40.0 °C |
16200 psi @Strain 1.20 %, Temperature -40.0 °F |
ISO 527 | |||
120 MPa @Strain 1.60 %, Temperature 0.000 °C |
17400 psi @Strain 1.60 %, Temperature 32.0 °F |
ISO 527 | |||
129 MPa @Strain 1.83 %, Temperature 0.000 °C |
18700 psi @Strain 1.83 %, Temperature 32.0 °F |
ISO 527 | |||
130 MPa @Strain 1.44 %, Temperature -40.0 °C |
18900 psi @Strain 1.44 %, Temperature -40.0 °F |
ISO 527 | |||
136 MPa @Strain 2.05 %, Temperature 0.000 °C |
19700 psi @Strain 2.05 %, Temperature 32.0 °F |
ISO 527 | |||
142 MPa @Strain 2.28 %, Temperature 0.000 °C |
20600 psi @Strain 2.28 %, Temperature 32.0 °F |
ISO 527 | |||
146 MPa @Strain 1.69 %, Temperature -40.0 °C |
21200 psi @Strain 1.69 %, Temperature -40.0 °F |
ISO 527 | |||
160 MPa @Strain 1.93 %, Temperature -40.0 °C |
23200 psi @Strain 1.93 %, Temperature -40.0 °F |
ISO 527 | |||
172 MPa @Strain 2.17 %, Temperature -40.0 °C |
24900 psi @Strain 2.17 %, Temperature -40.0 °F |
ISO 527 | |||
184 MPa @Strain 2.41 %, Temperature -40.0 °C |
26700 psi @Strain 2.41 %, Temperature -40.0 °F |
ISO 527 | |||
Elongation at Break | 3.0 % @Temperature -40.0 °C |
3.0 % @Temperature -40.0 °F |
ASTM D638 | ||
3.3 % @Temperature 23.0 °C |
3.3 % @Temperature 73.4 °F |
ASTM D638 | |||
3.3 % @Temperature 23.0 °C |
3.3 % @Temperature 73.4 °F |
ISO 527 | |||
7.0 % @Temperature 90.0 °C |
7.0 % @Temperature 194 °F |
ASTM D638 | |||
7.5 % @Temperature 150 °C |
7.5 % @Temperature 302 °F |
ASTM D638 | |||
Tensile Modulus | 2.70 GPa @Temperature 150 °C |
392 ksi @Temperature 302 °F |
ASTM D638 | ||
3.28 GPa @Temperature 90.0 °C |
476 ksi @Temperature 194 °F |
ASTM D638 | |||
9.30 GPa @Temperature 23.0 °C |
1350 ksi @Temperature 73.4 °F |
ISO 527 | |||
9.31 GPa @Temperature 23.0 °C |
1350 ksi @Temperature 73.4 °F |
ASTM D638 | |||
9.79 GPa @Temperature -40.0 °C |
1420 ksi @Temperature -40.0 °F |
ASTM D638 | |||
Flexural Strength | 60.0 MPa @Temperature 150 °C |
8700 psi @Temperature 302 °F |
ASTM D790 | ||
86.2 MPa @Temperature 90.0 °C |
12500 psi @Temperature 194 °F |
ASTM D790 | |||
193 MPa @Temperature 23.0 °C |
28000 psi @Temperature 73.4 °F |
ASTM D790 | |||
266 MPa @Temperature -40.0 °C |
38600 psi @Temperature -40.0 °F |
ASTM D790 | |||
Flexural Modulus | 2.25 GPa @Temperature 150 °C |
326 ksi @Temperature 302 °F |
ASTM D790 | ||
2.30 GPa @Temperature 150 °C |
334 ksi @Temperature 302 °F |
ISO 178 | |||
3.00 GPa @Temperature 93.0 °C |
435 ksi @Temperature 199 °F |
ISO 178 | |||
3.01 GPa @Temperature 90.0 °C |
437 ksi @Temperature 194 °F |
ASTM D790 | |||
7.83 GPa @Temperature 23.0 °C |
1140 ksi @Temperature 73.4 °F |
ISO 178 | |||
8.28 GPa @Temperature 23.0 °C |
1200 ksi @Temperature 73.4 °F |
ASTM D790 | |||
8.90 GPa @Temperature -40.0 °C |
1290 ksi @Temperature -40.0 °F |
ASTM D790 | |||
8.90 GPa @Temperature -40.0 °C |
1290 ksi @Temperature -40.0 °F |
ISO 178 | |||
Compressive Strength | 148 MPa @Temperature 23.0 °C |
21500 psi @Temperature 73.4 °F |
ASTM D695 | ||
Izod Impact, Notched | 1.01 J/cm @Temperature -40.0 °C |
1.89 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | ||
1.33 J/cm @Temperature 23.0 °C |
2.49 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |||
Izod Impact, Unnotched | 9.60 J/cm @Temperature -40.0 °C |
18.0 ft-lb/in @Temperature -40.0 °F |
ASTM D4812 | ||
9.60 J/cm @Temperature 23.0 °C |
18.0 ft-lb/in @Temperature 73.4 °F |
ASTM D4812 | |||
Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | ||
Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | ||
8.60 J/cm² @Temperature -30.0 °C |
40.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+15 ohm-cm @Temperature 23.0 °C |
1.00e+15 ohm-cm @Temperature 73.4 °F |
ASTM D257 | ||
1.00e+15 ohm-cm @Temperature 23.0 °C |
1.00e+15 ohm-cm @Temperature 73.4 °F |
IEC 60093 | |||
Surface Resistance | 1.00e+14 ohm @Temperature 23.0 °C |
1.00e+14 ohm @Temperature 73.4 °F |
ASTM D257 | ||
1.00e+14 ohm @Temperature 23.0 °C |
1.00e+14 ohm @Temperature 73.4 °F |
IEC 60093 | |||
Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
3.3 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
ASTM D150 | ||
3.3 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
3.3 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
IEC 60250 | |||
3.4 @Frequency 1000 Hz, Temperature 23.0 °C |
3.4 @Frequency 1000 Hz, Temperature 73.4 °F |
ASTM D150 | |||
4.2 @Frequency 100 Hz, Temperature 23.0 °C |
4.2 @Frequency 100 Hz, Temperature 73.4 °F |
IEC 60250 | |||
Dielectric Strength | 12.0 kV/mm @Thickness 3.20 mm, Temperature 150 °C |
305 kV/in @Thickness 0.126 in, Temperature 302 °F |
500 V/s, in oil; Short Time; ASTM D149 | ||
14.5 kV/mm @Thickness 1.60 mm, Temperature 150 °C |
368 kV/in @Thickness 0.0630 in, Temperature 302 °F |
500 V/s, in oil; Short Time; ASTM D149 | |||
17.5 kV/mm @Thickness 3.20 mm, Temperature 95.0 °C |
445 kV/in @Thickness 0.126 in, Temperature 203 °F |
500 V/s, in oil; Short Time; ASTM D149 | |||
21.5 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C |
546 kV/in @Thickness 0.126 in, Temperature 73.4 °F |
500 V/s, in oil; Short Time; ASTM D149 | |||
24.0 kV/mm @Thickness 1.60 mm, Temperature 95.0 °C |
610 kV/in @Thickness 0.0630 in, Temperature 203 °F |
500 V/s, in oil; Short Time; ASTM D149 | |||
26.5 kV/mm @Thickness 1.60 mm, Temperature 23.0 °C |
673 kV/in @Thickness 0.0630 in, Temperature 73.4 °F |
500 V/s, in oil; Short Time; ASTM D149 | |||
Dissipation Factor | 0.010 @Frequency 1000 Hz, Temperature 23.0 °C |
0.010 @Frequency 1000 Hz, Temperature 73.4 °F |
ASTM D150 | ||
0.015 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
0.015 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
ASTM D150 | |||
0.015 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
0.015 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
IEC 60250 | |||
Comparative Tracking Index | 325 V @Thickness 3.00 mm, Temperature 23.0 °C |
325 V @Thickness 0.118 in, Temperature 73.4 °F |
UL 746A | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
ASTM E 831 | ||
500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
ASTM E 831 | |||
500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
ASTM E 831 | |||
500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |||
500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |||
500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
ISO 11359-1/-2 | |||
500 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ASTM E 831 | |||
500 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |||
CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
47.2 µin/in-°F @Temperature -40.0 - 73.4 °F |
ASTM E 831 | ||
85.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 131 °F |
ASTM E 831 | |||
85.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
47.2 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |||
85.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |||
92.0 µm/m-°C @Temperature 55.0 - 160 °C |
51.1 µin/in-°F @Temperature 131 - 320 °F |
ASTM E 831 | |||
92.0 µm/m-°C @Temperature 55.0 - 160 °C |
51.1 µin/in-°F @Temperature 131 - 320 °F |
ISO 11359-1/-2 | |||
122 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
67.8 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ASTM E 831 | |||
122 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
67.8 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |||
Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 | ||
254 °C | 489 °F | ASTM D3418 | |||
Deflection Temperature at 0.46 MPa (66 psi) | 237 °C | 459 °F | ISO 75-1/-2 | ||
240 °C | 464 °F | ASTM D648 | |||
Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
220 °C | 428 °F | ASTM D648 | |||
UL RTI, Electrical | 140 °C @Thickness 0.750 mm |
284 °F @Thickness 0.0295 in |
UL 746B | ||
140 °C @Thickness 1.50 mm |
284 °F @Thickness 0.0591 in |
UL 746B | |||
140 °C @Thickness 3.00 mm |
284 °F @Thickness 0.118 in |
UL 746B | |||
UL RTI, Mechanical with Impact | 140 °C @Thickness 3.00 mm |
284 °F @Thickness 0.118 in |
UL 746B | ||
140 °C @Thickness 1.50 mm |
284 °F @Thickness 0.0591 in |
UL 746B | |||
140 °C @Thickness 0.750 mm |
284 °F @Thickness 0.0295 in |
UL 746B | |||
UL RTI, Mechanical without Impact | 140 °C @Thickness 3.00 mm |
284 °F @Thickness 0.118 in |
UL 746B | ||
140 °C @Thickness 0.750 mm |
284 °F @Thickness 0.0295 in |
UL 746B | |||
140 °C @Thickness 1.50 mm |
284 °F @Thickness 0.0591 in |
UL 746B | |||
Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |||
HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 | |||
HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL94 | |||
HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL94 | |||
HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL94 | |||
Oxygen Index | 22 % | 22 % | ISO 4589-1/-2 | ||
Processing Properties | Metric | English | Comments | ||
Melt Temperature | 280 °C | 536 °F | Optimum | ||
270 - 290 °C | 518 - 554 °F | ||||
Mold Temperature | >= 95.0 °C | >= 203 °F | |||
110 °C | 230 °F | optimum | |||
Drying Temperature | 120 °C | 248 °F | |||
Dry Time | 4.00 hour | 4.00 hour | |||
Moisture Content | <= 0.020 % | <= 0.020 % | |||
De |
|||||
Additive | Impact Modifier | ||||
Appearance | Natural Color | ||||
Drying Recommended | Yes | ||||
Features | Impact Modified | ||||
Impact Resistance, Good | |||||
Stiffness, Good | |||||
Strength, Good | |||||
Thermal Aging Resistance, Good | |||||
Filler | Glass fiber reinforcement | ||||
Generic | PET | ||||
Heat Stabilized | Yes | ||||
Material Status | Current | ||||
Part Marking Code | >PET-IGF30< | ISO 11469 | |||
Polymer Family | Polyester | ||||
Polymer Type | PET | ||||
Processing Method | Injection Molding | ||||
Product Category | Glass Reinforced Resins | ||||
Toughened Resins | |||||
Resin Identification | PET-IGF30 | ISO 1043 | |||
RoHS Compliance | Contact Manufacturer | ||||
Ultrasonic Weldable | Yes | ||||
Uses | Automotive Applications | ||||
Housings | |||||
Structural Parts |
上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com