沙伯基础创新塑料XENOY®x2420,10%玻璃填充,高流动

沙伯基础创新塑料XENOY®x2420,PC+POLYESTER(亚太) 类别:聚合物;热塑性塑料;聚碳酸酯(聚碳酸酯);聚碳酸酯/聚酯共混物;聚酯,茶多酚;聚对苯二甲酸乙二醇酯(聚酯) 材料说明:Xenoy * x2420是10%玻璃填充,高流动,冲击改性,注射模压级设计的高流动性和冲击强度。x2420提高熔体流动性、冲击韧性和广阔的色彩空间
 物性表:
 
Physical Properties Metric English Comments
Specific Gravity  1.28 g/cc 1.28 g/cc ASTM D792
Density  1.28 g/cc 0.0462 lb/in³ ISO 1183
Moisture Absorption  0.0400 % 0.0400 % 23°C / 50% RH; ISO 62
Water Absorption at Saturation  0.020 % 0.020 % ISO 62
Linear Mold Shrinkage, Flow  0.0015 - 0.0025 cm/cm
@Thickness 3.20 mm
0.0015 - 0.0025 in/in
@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse  0.0030 - 0.0040 cm/cm
@Thickness 3.20 mm
0.0030 - 0.0040 in/in
@Thickness 0.126 in
SABIC Method
Melt Index of Compound   12 g/10 min
@Load 2.16 kg,
Temperature 265 °C
12 g/10 min
@Load 4.76 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
  26 g/10 min
@Load 1.20 kg,
Temperature 300 °C
26 g/10 min
@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  35.0 MPa 5080 psi Type I, 5 mm/min; ASTM D638
  37.0 MPa 5370 psi 5 mm/min; ISO 527
Tensile Strength, Yield  50.0 MPa 7250 psi Type I, 5 mm/min; ASTM D638
  51.0 MPa 7400 psi 5 mm/min; ISO 527
Elongation at Break  7.0 % 7.0 % 5 mm/min; ISO 527
Elongation at Yield  3.0 % 3.0 % 5 mm/min; ISO 527
  3.0 % 3.0 % Type I, 5 mm/min; ASTM D638
Tensile Modulus  3.80 GPa 551 ksi 5 mm/min; ASTM D638
Flexural Yield Strength  90.0 MPa 13100 psi 1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus  3.50 GPa 508 ksi 1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched  2.05 J/cm 3.84 ft-lb/in ASTM D256
Izod Impact, Unnotched  16.0 J/cm 30.0 ft-lb/in ASTM D4812
Izod Impact, Notched (ISO)  14.0 kJ/m² 6.66 ft-lb/in² 80*10*4; ISO 180/1A
  8.00 kJ/m²
@Temperature -30.0 °C
3.81 ft-lb/in²
@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO)  110 kJ/m² 52.3 ft-lb/in² 80*10*4; ISO 180/1U
  74.0 kJ/m²
@Temperature -30.0 °C
35.2 ft-lb/in²
@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched  9.50 J/cm² 45.2 ft-lb/in² Edgew 80*10*4 sp=62mm; ISO 179/1eU
  9.50 J/cm²
@Temperature -30.0 °C
45.2 ft-lb/in²
@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched  1.50 J/cm² 7.14 ft-lb/in² Edgew 80*10*4 sp=62mm; ISO 179/1eA
  0.700 J/cm²
@Temperature -30.0 °C
3.33 ft-lb/in²
@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy  36.0 J
@Temperature 23.0 °C
26.6 ft-lb
@Temperature 73.4 °F
ASTM D3763
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow   40.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
22.2 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
  50.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow   80.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
  90.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
50.0 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)  111 °C
@Thickness 3.20 mm
232 °F
@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)  101 °C
@Thickness 3.20 mm
214 °F
@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point  118 °C 244 °F Rate B/120; ISO 306
UL RTI, Electrical  75.0 °C 167 °F UL 746B
UL RTI, Mechanical with Impact  75.0 °C 167 °F UL 746B
UL RTI, Mechanical without Impact  75.0 °C 167 °F UL 746B
Flammability, UL94  HB
@Thickness 0.400 mm
HB
@Thickness 0.0157 in
UL 94
 

0..

上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41499.html

免责声明: 本文 沙伯基础创新塑料XENOY®x2420,10%玻璃填充,高流动 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4