日本出光/7020 SPS,20%玻璃填充

日本出光/7020 SPS,20%玻璃填充 类别:聚合物;热塑性的;聚苯乙烯(PS);间规聚苯乙烯(SPS);间规聚苯乙烯(SPS)与玻璃纤维或碳纤维 材质说明:结晶性聚合物共混,玻璃填充,冲击改性。用于汽车电子应用。
 物性表:

 
Physical Properties Metric English Comments
Density  1.25 g/cc 0.0452 lb/in³  
Filler Content  20 % 20 %  
Water Absorption  0.22 % 0.22 % 24 hrs., 50% RH
Linear Mold Shrinkage, Flow  0.0030 - 0.0060 cm/cm 0.0030 - 0.0060 in/in  
Linear Mold Shrinkage, Transverse  0.0050 - 0.0080 cm/cm 0.0050 - 0.0080 in/in  
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  150 MPa 21800 psi  
Elongation at Break  2.9 % 2.9 %  
Tensile Modulus  7.30 GPa 1060 ksi  
Flexural Yield Strength  215 MPa 31200 psi  
Flexural Modulus  6.70 GPa 972 ksi  
Izod Impact, Notched (ISO)  8.00 kJ/m² 3.81 ft-lb/in²  
Izod Impact, Unnotched (ISO)  45.0 kJ/m² 21.4 ft-lb/in²  
Charpy Impact Unnotched  5.50 J/cm² 26.2 ft-lb/in²  
Charpy Impact, Notched  0.900 J/cm² 4.28 ft-lb/in²  
 
Electrical Properties Metric English Comments
Electrical Resistivity  3.10e+15 ohm-cm 3.10e+15 ohm-cm  
Dielectric Constant  3.1 3.1  
Dielectric Strength  25.0 kV/mm 635 kV/in ASTM D145
Dissipation Factor  0.034 0.034 IEC 60250
Arc Resistance  120 - 180 sec 120 - 180 sec ASTM D495
Comparative Tracking Index  400 - 600 V 400 - 600 V IEC 60112
Hot Wire Ignition, HWI  0.00 - 7.0 sec
@Thickness 1.50 mm
0.00 - 7.0 sec
@Thickness 0.0591 in
UL 746A
High Amp Arc Ignition, HAI  >= 120 arcs
@Thickness 1.50 mm
>= 120 arcs
@Thickness 0.0591 in
UL 746A
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  30.0 µm/m-°C
@Temperature -30.0 - 30.0 °C
16.7 µin/in-°F
@Temperature -22.0 - 86.0 °F
 
CTE, linear, Transverse to Flow  54.0 µm/m-°C 30.0 µin/in-°F  
Deflection Temperature at 0.46 MPa (66 psi)  240 °C 464 °F  
Deflection Temperature at 1.8 MPa (264 psi)  260 °C 500 °F  
UL RTI, Electrical  50.0 °C 122 °F UL746B
UL RTI, Mechanical with Impact  50.0 °C 122 °F UL746B
UL RTI, Mechanical without Impact  50.0 °C 122 °F UL746B
Flammability, UL94  HB
@Thickness 0.750 mm
HB
@Thickness 0.0295 in
 
 
Processing Properties Metric English Comments
Melt Temperature  280 - 310 °C 536 - 590 °F  
Mold Temperature  50.0 - 80.0 °C 122 - 176 °F  
Drying Temperature  80.0 °C 176 °F 1 - 3 hrs
 
Descriptive Properties
Comments High Ductility  
  Nylon/SPS blend

.0..
上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com
 
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41529.html

免责声明: 本文 日本出光/7020 SPS,20%玻璃填充 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4