拜耳PC/PET UT305 良好的外观和优异的尺寸稳定性

拜耳PC/PET UT305 共混 类别:聚合物;热塑性;聚碳酸酯(PC);聚碳酸酯/聚酯共混物;聚酯,聚对苯二甲酸乙二醇酯;聚对苯二甲酸乙二醇酯(聚酯) 材料说明:PC +PET-共混物,易释放,注塑成型。makroblend ut305具有高耐热性,良好的耐化学性和流动性。成型零件从ut305提供一个良好的外观和优异的尺寸稳定性,即使在高湿度的环境中。
物性表:
 
Physical Properties Metric English Comments
Density  1.24 g/cc 0.0448 lb/in³ ISO 1183-1
Moisture Absorption at Equilibrium  0.250 % 0.250 % 50% RH; ISO 62
Water Absorption at Saturation  0.550 % 0.550 % ISO 62
Linear Mold Shrinkage, Flow  0.00100 cm/cm 0.00100 in/in Post; b.o. ISO 2577
  0.0065 cm/cm 0.0065 in/in b.o. ISO 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  54.0 MPa 7830 psi 50 mm/min; ISO 527-1,-2
Tensile Strength, Yield  70.0 MPa 10200 psi 50 mm/min; ISO 527-1,-2
Elongation at Break  110 % 110 % 50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield  5.5 % 5.5 % 50 mm/min; ISO 527-1,-2
  6.20 % 6.20 % Flexural strain, 2 mm/min; ISO 178
Tensile Modulus  2.60 GPa 377 ksi 1 mm/min; ISO 527-1,-2
Flexural Strength  100 MPa 14500 psi 2 mm/min; ISO 178
Flexural Yield Strength  82.0 MPa
@Strain 3.50 %
11900 psi
@Strain 3.50 %
2 mm/min; ISO 178
Flexural Modulus  2.60 GPa 377 ksi 2 mm/min; ISO 178
Izod Impact, Notched (ISO)   6.00 kJ/m²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
ISO 180-A
  7.00 kJ/m²
@Temperature 23.0 °C
3.33 ft-lb/in²
@Temperature 73.4 °F
ISO 180-A
  8.00 kJ/m²
@Temperature 23.0 °C
3.81 ft-lb/in²
@Temperature 73.4 °F
ISO 180-A
  8.00 kJ/m²
@Temperature -30.0 °C
3.81 ft-lb/in²
@Temperature -22.0 °F
ISO 180-A
Izod Impact, Unnotched (ISO)   NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
ISO 180-U
  NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
ISO 180-U
Charpy Impact Unnotched   NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
ISO 179-1eU
  NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
ISO 179-1eU
Charpy Impact, Notched   0.600 J/cm²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
ISO 179-1eA
  0.800 J/cm²
@Temperature 23.0 °C
3.81 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1eA
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  70.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
38.9 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 1135-1,-2
CTE, linear, Transverse to Flow  70.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
38.9 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 1135-1,-2
Deflection Temperature at 0.46 MPa (66 psi)  128 °C 262 °F ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi)  108 °C 226 °F ISO 75-1,-2
Vicat Softening Point  140 °C
@Load 5.10 kg
284 °F
@Load 11.2 lb
120°C/h; ISO 306
UL RTI, Electrical  75.0 °C 167 °F UL 746B
UL RTI, Mechanical with Impact  75.0 °C 167 °F UL 746B
UL RTI, Mechanical without Impact  75.0 °C 167 °F UL 746B
Flammability, UL94  HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
 
 
Processing Properties Metric English Comments
Injection Velocity  200 mm/sec 7.87 in/sec ISO 294
 

图:


上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41566.html

免责声明: 本文 拜耳PC/PET UT305 良好的外观和优异的尺寸稳定性 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4