拜耳 UT4045 G PC/PBT共混物,20% 玻璃纤维增强

拜耳 UT4045 G PC/PBT共混物,20% 玻璃纤维增强 类别:聚合物;热塑性的;聚碳酸酯(PC);聚碳酸酯/聚对苯二甲酸丁二醇酯(PBT)的共混物,Glass Filled;聚酯,TP;聚对苯二甲酸丁二醇酯(PBT) 材料说明:(PBT)的混纺,20%玻璃纤维增强,易释放,注射成型。具有高刚度、优良的耐化学性,良好的流动性和优异的尺寸稳定性
物性表:
 
Physical Properties Metric English Comments
Density  1.40 g/cc 0.0506 lb/in³ ISO 1183-1
Filler Content  20.0 % 20.0 % Method A; b.o. ISO 3451-1
Moisture Absorption at Equilibrium  0.150 % 0.150 % ISO 62
Water Absorption at Saturation  0.300 % 0.300 % ISO 62
Linear Mold Shrinkage, Flow  0.00200 - 0.00400 cm/cm 0.00200 - 0.00400 in/in 150x105x3 mm; 260 °C / MT 80 °C; 600 bar; b.o. ISO 2577
  0.00200 - 0.00600 cm/cm 0.00200 - 0.00600 in/in b.o. ISO 2577
Linear Mold Shrinkage, Transverse  0.00500 - 0.00700 cm/cm 0.00500 - 0.00700 in/in 150x105x3 mm; 260 °C / MT 80 °C; 600 bar; b.o. ISO 2577
Melt Flow  42.0 g/10 min
@Load 5.00 kg,
Temperature 260 °C
42.0 g/10 min
@Load 11.0 lb,
Temperature 500 °F
ISO 1133
 
Mechanical Properties Metric English Comments
Ball Indentation Hardness  90.0 MPa 13100 psi ISO 2039-1
Tensile Strength at Break  100 MPa 14500 psi 5 mm/min; ISO 527-1,-2
Tensile Strength, Yield  100 MPa 14500 psi 50 mm/min; ISO 527-1,-2
Elongation at Break  3.0 % 3.0 % 5 mm/min; ISO 527-1,-2
  3.0 % 3.0 % Nominal, 5 mm/min; ISO 527-1,-2
Elongation at Yield  3.0 % 3.0 % 50 mm/min; ISO 527-1,-2
  3.00 % 3.00 % Flexural strain, 2 mm/min; ISO 178
Tensile Modulus  6.50 GPa 943 ksi 1 mm/min; ISO 527-1,-2
Flexural Strength  160 MPa 23200 psi 2 mm/min; ISO 178
Flexural Modulus  6.10 GPa 885 ksi 2 mm/min; ISO 178
Izod Impact, Notched (ISO)   6.00 kJ/m²
@Temperature 23.0 °C
2.86 ft-lb/in²
@Temperature 73.4 °F
ISO 180-A
  6.00 kJ/m²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
ISO 180-A
Izod Impact, Unnotched (ISO)   35.0 kJ/m²
@Temperature -30.0 °C
16.7 ft-lb/in²
@Temperature -22.0 °F
ISO 180-U
  40.0 kJ/m²
@Temperature 23.0 °C
19.0 ft-lb/in²
@Temperature 73.4 °F
ISO 180-U
Charpy Impact Unnotched   4.00 J/cm²
@Temperature -30.0 °C
19.0 ft-lb/in²
@Temperature -22.0 °F
ISO 179-1eU
  4.50 J/cm²
@Temperature 23.0 °C
21.4 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1eU
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  >= 1.00e+17 ohm >= 1.00e+17 ohm IEC 60093
Dielectric Constant   0.150
@Frequency 1.00e+6 Hz
0.150
@Frequency 1.00e+6 Hz
IEC 60250
  3.60
@Frequency 100 Hz
3.60
@Frequency 100 Hz
IEC 60250
Dielectric Strength  33.0 kV/mm
@Thickness 1.00 mm
838 kV/in
@Thickness 0.0394 in
IEC 60243-1
Dissipation Factor   0.00130
@Frequency 100 Hz
0.00130
@Frequency 100 Hz
IEC 60250
  0.0144
@Frequency 1.00e+6 Hz
0.0144
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index  175 V 175 V Solution A; IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  70.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
38.9 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow  35.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
19.4 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi)  130 °C 266 °F ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi)  110 °C 230 °F ISO 75-1,-2
Vicat Softening Point  140 °C
@Load 5.10 kg
284 °F
@Load 11.2 lb
120°C/h; ISO 306
Shrinkage  <= 0.10 % <= 0.10 % post-shrinkage; b.o. ISO 2577
 
Processing Properties Metric English Comments
Melt Temperature  260 °C 500 °F Injection molding; ISO 294
Mold Temperature  70.0 °C 158 °F Injection molding; ISO 294
Injection Velocity  200 mm/sec 7.87 in/sec ISO 294
 

图:


上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41567.html

免责声明: 本文 拜耳 UT4045 G PC/PBT共混物,20% 玻璃纤维增强 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4