Availability
|
|
Features
|
|
Appearance
|
|
Forms
|
|
Physical |
Nominal Value
|
Unit
|
Test Method
|
Specific Gravity
|
1.28
|
g/cm³
|
ASTM D792 |
Molding Shrinkage - Flow
|
0.90 to 1.2
|
%
|
ASTM D955 |
Water Absorption (24 hr)
|
1.0
|
%
|
ASTM D570 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Strength (Yield)
|
64.1
|
MPa
|
ASTM D638 |
Tensile Elongation (Break)
|
10
|
%
|
ASTM D638 |
Flexural Modulus
|
2620
|
MPa
|
ASTM D790 |
Flexural Strength (Yield)
|
110
|
MPa
|
ASTM D790 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Notched Izod Impact (23°C, 3.18 mm)
|
43
|
J/m
|
ASTM D256 |
Tensile Impact Strength
|
137
|
kJ/m²
|
ASTM D1822 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Deflection Temperature Under Load
|
ASTM D648 | ||
0.45 MPa, Unannealed
|
193
|
°C
|
|
1.8 MPa, Unannealed
|
76.7
|
°C
|
|
Melting Temperature
|
249 to 260
|
°C
|
|
CLTE - Flow
|
0.000077
|
cm/cm/°C
|
ASTM D696 |
RTI Elec (1.47 mm)
|
65.0
|
°C
|
UL 746 |
RTI Imp (1.47 mm)
|
65.0
|
°C
|
UL 746 |
RTI Str (1.47 mm)
|
65.0
|
°C
|
UL 746 |
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Arc Resistance
|
104
|
sec
|
ASTM D495 |
High Amp Arc Ignition (HAI)
|
200
|
|
UL 746 |
High Voltage Arc Tracking Rate (HVTR)
|
12.7
|
mm/min
|
UL 746 |
Hot-wire Ignition (HWI)
|
8.0
|
sec
|