Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Features
|
|
|||
|
Forms
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.39
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
0.30 to 0.60
|
%
|
Internal Method |
|
Water Absorption (23°C, 24 hr)
|
1.7
|
%
|
ISO 62 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress (Yield)
|
230
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
3.0
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
9100
|
MPa
|
ISO 178 |
|
Flexural Strength
|
310
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact Strength (23°C)
|
24
|
kJ/m²
|
ISO 180 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
0.45 MPa, Unannealed
|
260
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
250
|
°C
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
265
|
°C
|
ISO 3146 |
| Flammability |
Nominal Value
|
|
Test Method
|
|
Flame Rating
|
HB
|
|
UL 94 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
90.0 to 100
|
°C
|
|
|
Drying Time
|
2.0 to 4.0
|
hr
|
|
|
Processing (Melt) Temp
|
240 to 270
|
°C
|
|
|
Mold Temperature
|
50.0 to 100
|
°C
|
|
|
Injection Pressure
|
30.0 to 80.0
|
MPa
|