Availability
|
|
|||
Additive
|
|
|||
Features
|
|
|||
Uses
|
|
|||
Appearance
|
|
|||
Resin ID (ISO 1043)
|
|
Physical | Dry | Conditioned |
Unit
|
Test Method
|
Density (23°C)
|
1.14
|
--
|
g/cm³
|
ISO 1183 |
Spiral Flow 3, 4
|
104
|
--
|
cm
|
Internal Method |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow
|
2.3
|
--
|
%
|
|
Flow
|
1.9
|
--
|
%
|
|
Water Absorption (Saturation, 23°C)
|
8.0 to 9.0
|
--
|
%
|
ISO 62 |
Humidity Absorption - 62% RH (70°C)
|
2.9 to 3.1
|
--
|
%
|
ISO 1110 |
Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
Tensile Modulus
|
3100
|
1100
|
MPa
|
ISO 527-2/1 |
Tensile Stress (Yield)
|
85.0
|
50.0
|
MPa
|
ISO 527-2/50 |
Tensile Strain
|
ISO 527-2/50 | |||
Yield
|
4.5
|
20
|
%
|
|
Break
|
> 25
|
> 50
|
%
|
|
Flexural Modulus 5
|
2800
|
--
|
MPa
|
ISO 178 |
Flexural Strength 5
|
110
|
--
|
MPa
|
ISO 178 |
Impact | Dry | Conditioned |
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
-30°C
|
2.0
|
--
|
kJ/m²
|
|
23°C
|
3.0
|
13
|
kJ/m²
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
-30°C
|
No Break
|
--
|
|
|
23°C
|
No Break
|
No Break
|
|
Thermal | Dry | Conditioned |
Unit
|
Test Method
|
Heat Deflection Temperature
|
||||
0.45 MPa, Unannealed
|
215
|
--
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
75.0
|
--
|
°C
|
ISO 75-2/A |
Melting Temperature 6
|
262
|
--
|
°C
|
DIN EN 11357-1 |
CLTE
|
ISO 11359-2 | |||
Flow: 23 to 80°C
|
0.000071
|
--
|
cm/cm/°C
|
|
Transverse: 23 to 80°C
|
0.00011
|
--
|
cm/cm/°C
|
Electrical | Dry | Conditioned |
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+13
|
--
|
ohm
|
IEC 60093 |
Volume Resistivity
|
1.0E+13
|
--
|
ohm·cm
|
IEC 60093 |
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
Flammability | Dry | Conditioned |
Unit
|
Test Method
|
Burning Rate 7 (1.00 mm)
|
< 100
|
--
|
mm/min
|
FMVSS 302 |
Flame Rating (0.800 mm)
|
V-2
|
--
|
|
UL 94 |
Glow Wire Flammability Index (1.60 mm)
|
750
|
--
|
°C
|
IEC 60695-2-12 |
Glow Wire Ignition Temperature (1.60 mm)
|
675
|
--
|
°C
|
IEC 60695-2-13 |