Availability
|
|
|||
Filler / Reinforcement
|
|
|||
Features
|
|
|||
Uses
|
|
|||
Appearance
|
|
|||
Resin ID (ISO 1043)
|
|
Physical | Dry | Conditioned |
Unit
|
Test Method
|
Density (23°C)
|
1.40
|
--
|
g/cm³
|
ISO 1183 |
Spiral Flow 2, 3
|
77.0
|
--
|
cm
|
Internal Method |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow
|
1.3
|
--
|
%
|
|
Flow
|
0.17
|
--
|
%
|
|
Water Absorption (Saturation, 23°C)
|
4.7 to 5.3
|
--
|
%
|
ISO 62 |
Humidity Absorption - 62% RH (70°C)
|
1.8 to 2.0
|
--
|
%
|
ISO 1110 |
Hardness | Dry | Conditioned |
Unit
|
Test Method
|
Ball Indentation Hardness (H 961/30)
|
255
|
--
|
MPa
|
ISO 2039-1 |
Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
Tensile Modulus
|
11600
|
8400
|
MPa
|
ISO 527-2/1 |
Tensile Stress (Break)
|
215
|
145
|
MPa
|
ISO 527-2/5 |
Tensile Strain (Break)
|
3.0
|
5.0
|
%
|
ISO 527-2/5 |
Flexural Modulus 4
|
10000
|
8000
|
MPa
|
ISO 178 |
Flexural Strength 4
|
300
|
245
|
MPa
|
ISO 178 |
Impact | Dry | Conditioned |
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
-30°C
|
13
|
--
|
kJ/m²
|
|
23°C
|
15
|
19
|
kJ/m²
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
-30°C
|
90
|
--
|
kJ/m²
|
|
23°C
|
92
|
100
|
kJ/m²
|
Thermal | Dry | Conditioned |
Unit
|
Test Method
|
Heat Deflection Temperature
|
||||
0.45 MPa, Unannealed
|
260
|
--
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
255
|
--
|
°C
|
ISO 75-2/A |
8.0 MPa, Unannealed
|
220
|
--
|
°C
|
ISO 75-2/C |
Melting Temperature 5
|
262
|
--
|
°C
|
DIN EN 11357-1 |
Electrical | Dry | Conditioned |
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+13
|
--
|
ohm
|
IEC 60093 |
Volume Resistivity
|
1.0E+14
|
--
|
ohm·cm
|
IEC 60093 |
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
Flammability | Dry | Conditioned |
Unit
|
Test Method
|
Burning Rate 6 (1.00 mm)
|
< 100
|
--
|
mm/min
|
FMVSS 302 |
Flame Rating (1.60 mm)
|
HB
|
--
|
|
UL 94 |
Glow Wire Flammability Index (1.60 mm)
|
650
|
--
|
°C
|
IEC 60695-2-12 |
Additional Information | Dry | Conditioned |
Unit
|
Test Method
|
Reinforcement Content
|
35
|
--
|
%
|
ISO 1172 |