Resin ID (ISO 1043)
|
|
Physical | Dry | Conditioned |
Unit
|
Test Method
|
Density (23°C)
|
1.07
|
--
|
g/cm³
|
ISO 1183 |
Spiral Flow 2, 3
|
77.0
|
--
|
cm
|
Internal Method |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow
|
1.4
|
--
|
%
|
|
Flow
|
1.4
|
--
|
%
|
|
Humidity Absorption - 62% RH (70°C)
|
1.7
|
--
|
%
|
ISO 1110 |
Hardness | Dry | Conditioned |
Unit
|
Test Method
|
Ball Indentation Hardness (H 358/30)
|
80.0
|
--
|
MPa
|
ISO 2039-1 |
Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
Tensile Modulus
|
2000
|
1200
|
MPa
|
ISO 527-2/1 |
Tensile Stress (Yield)
|
50.0
|
40.0
|
MPa
|
ISO 527-2/50 |
Tensile Strain
|
ISO 527-2/50 | |||
Yield
|
4.8
|
--
|
%
|
|
Break
|
> 50
|
> 100
|
%
|
|
Flexural Modulus 4
|
1950
|
--
|
MPa
|
ISO 178 |
Impact | Dry | Conditioned |
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
-40°C
|
35
|
--
|
kJ/m²
|
|
-30°C
|
45
|
35
|
kJ/m²
|
|
23°C
|
> 80
|
> 100
|
kJ/m²
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
-40°C
|
No Break
|
--
|
|
|
-30°C
|
No Break
|
No Break
|
|
|
23°C
|
No Break
|
No Break
|
|
Thermal | Dry | Conditioned |
Unit
|
Test Method
|
Heat Deflection Temperature
|
||||
0.45 MPa, Unannealed
|
152
|
--
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
62.0
|
--
|
°C
|
ISO 75-2/A |
Melting Temperature 5
|
262
|
--
|
°C
|
DIN EN 11357-1 |
Electrical | Dry | Conditioned |
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+14
|
--
|
ohm
|
IEC 60093 |
Volume Resistivity
|
1.0E+15
|
--
|
ohm·cm
|
IEC 60093 |
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |
Flammability | Dry | Conditioned |
Unit
|
Test Method
|
Burning Rate 6 (1.00 mm)
|
< 100
|
--
|
mm/min
|
FMVSS 302 |
Flame Rating (1.60 mm)
|
HB
|
--
|
|
UL 94 |