Physical | Dry | Conditioned |
Unit
|
Test Method
|
Density
|
1.14
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage
|
ISO 294-4 | |||
Across Flow
|
1.6
|
--
|
%
|
|
Flow
|
1.6
|
--
|
%
|
|
Water Absorption
|
ISO 62 | |||
Saturation, 23°C
|
8.5
|
--
|
%
|
|
Equilibrium, 23°C, 50% RH
|
2.3
|
--
|
%
|
Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
Tensile Modulus
|
3500
|
1500
|
MPa
|
ISO 527-2 |
Tensile Stress (Yield)
|
95.0
|
60.0
|
MPa
|
ISO 527-2 |
Tensile Strain (Yield)
|
3.5
|
20
|
%
|
ISO 527-2 |
Nominal Tensile Strain at Break
|
25
|
> 50
|
%
|
ISO 527-2 |
Flexural Modulus
|
2800
|
--
|
MPa
|
ISO 178 |
Flexural Strength
|
125
|
--
|
MPa
|
ISO 178 |
Impact | Dry | Conditioned |
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
-30°C
|
6.0
|
6.0
|
kJ/m²
|
|
23°C
|
6.0
|
12
|
kJ/m²
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
-30°C
|
No Break
|
No Break
|
|
|
23°C
|
No Break
|
No Break
|
|
Thermal | Dry | Conditioned |
Unit
|
Test Method
|
Heat Deflection Temperature
|
||||
0.45 MPa, Unannealed
|
225
|
--
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
80.0
|
--
|
°C
|
ISO 75-2/A |
Melting Temperature 3
|
260
|
--
|
°C
|
ISO 11357-3 |
CLTE
|
ISO 11359-2 | |||
Flow
|
0.00010
|
--
|
cm/cm/°C
|
|
Transverse
|
0.00010
|
--
|
cm/cm/°C
|
Electrical | Dry | Conditioned |
Unit
|
Test Method
|
Surface Resistivity
|
--
|
1.0E+14
|
ohm
|
IEC 60093 |
Volume Resistivity
|
1.0E+15
|
1.0E+12
|
ohm·cm
|
IEC 60093 |
Electric Strength
|
25
|
20
|
kV/mm
|
IEC 60243-1 |
Relative Permittivity
|
IEC 60250 | |||
100 Hz
|
3.20
|
10.0
|
|
|
1 MHz
|
3.00
|
4.00
|
|
|
Dissipation Factor
|
IEC 60250 | |||
100 Hz
|
0.0060
|
0.14
|
|
|
1 MHz
|
0.017
|
0.10
|
|
|
Comparative Tracking Index
|
600
|
600
|
V
|
IEC 60112 |
Flammability | Dry | Conditioned |
Unit
|
Test Method
|
Flammability Classification
|
IEC 60695-11-10, -20 | |||
1.50 mm
|
V-2
|
--
|
|
|
3.00 mm
|
V-2
|
--
|