Availability
|
|
Filler / Reinforcement
|
|
Forms
|
|
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density
|
1.41
|
--
|
g/cm³
|
ISO 1183 |
Molding Shrinkage - Flow
|
0.35
|
--
|
%
|
ISO 294-4 |
Water Absorption
|
ISO 62 | |||
Saturation, 23°C
|
5.5
|
--
|
%
|
|
Equilibrium, 23°C, 50% RH
|
1.6
|
--
|
%
|
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus
|
ISO 527-2 | |||
23°C
|
11500
|
8500
|
MPa
|
|
90°C
|
7100
|
--
|
MPa
|
|
120°C
|
5900
|
--
|
MPa
|
|
Tensile Stress
|
ISO 527-2 | |||
Break, 23°C
|
210
|
150
|
MPa
|
|
Break, 90°C
|
115
|
--
|
MPa
|
|
Break, 120°C
|
100
|
--
|
MPa
|
|
Tensile Strain (Break, 23°C)
|
3.0
|
5.0
|
%
|
ISO 527-2 |
Flexural Modulus
|
ISO 178 | |||
23°C
|
10500
|
7700
|
MPa
|
|
90°C
|
6900
|
--
|
MPa
|
|
Flexural Strength
|
ISO 178 | |||
23°C
|
270
|
205
|
MPa
|
|
90°C
|
180
|
--
|
MPa
|
|
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179 | |||
-30°C
|
7.0
|
--
|
kJ/m²
|
|
23°C
|
12
|
14
|
kJ/m²
|
|
Charpy Unnotched Impact Strength
|
ISO 179 | |||
-30°C
|
45
|
--
|
kJ/m²
|
|
23°C
|
55
|
70
|
kJ/m²
|
Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Heat Deflection Temperature
|
||||
0.45 MPa, Unannealed
|
255
|
--
|
°C
|
ISO 75-2/B |
1.8 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/A |
CLTE - Flow (23°C)
|
0.000029
|
--
|
cm/cm/°C
|
ISO 11359-2 |
Thermal Conductivity
|
0.29
|
--
|
W/m/K
|
ISO 8302 |
Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+12
|
--
|
ohm
|
ASTM D257 |
Electric Strength (2.00 mm)
|
36
|
32
|
kV/mm
|
IEC 60243-1 |
Comparative Tracking Index
|
500
|
500
|
V
|
IEC 60112 |
Flammability |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating (1.60 mm)
|
HB
|
--
|
|
UL 94 |
Additional Information | ||||
Dry
|
The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods.
The value listed as Coefficient of Linear Thermal Expansion, Flow ISO 11359-1-2, was tested in accordance with ISO 7991. |